Abstract:The inhibition effects of silicate and molybdate on the corrosion of stainless steel 316 (SS 316) in neutral corrosive solution are reported. The neutral solution contains chloride, sulfate and bicarbonate ions with pH = 7.86. The inhibition effect of molybdate, silicate and silicate—molybdate composite on the corrosion of SS 316 was tested comparatively as a heuristic guidance, then a simulated investigation in an autoclave at 200 °C was conducted. The surface morphology of corroded samples is analyzed by optical microscope and macroscopic views, and XPS test is employed to detect the surface scales of corroded samples. The results show that molybdate, silicate and their composite show good inhibition effect on SS 316 in the neutral environment, the corrosion current density (CCD) in the electrochemical test (ECT) is reduced to I0 = −7.6047 E-08 as 250 mg l−1 silicate is added, while the CCD in the ECT decreased to I0 = −1.6915 E-07 Amp cm−2 as the composite of 200 mg l−1 silicate and 50 mg l−1 molybdate is added, which is much less than the CCD in the ECT I0 = −5.0235 E-07 Amp cm−2 without any inhibitor added; XPS analysis indicates that iron oxide formed on the surface of the sample in the neutral corrosive solution without any inhibitor and pitting was observed clearly; While the XPS analysis indicates that there forms iron molybdate and iron oxide on the surface of the sample in the neutral corrosive solution with addition of molybdate 200 mg l−1 and less pitting was observed; Moreover XPS analysis indicates that there were iron molybdate and silicate deposition on the surface of the sample in the neutral corrosive solution with adding silicate 200 mg l−1 and molybdate 50 mg l−1 without pitting trace. Comprehensive consideration, the proper amount of inhibitors could be addition of 250 mg l−1 silicate or combination of 200 mg l−1 silicate and 50 mg l−1 molybdate composite.

Inhibition Performance of Sodium Diethyl Dithiocarbamate and Its Compounding Inhibitors for 316L Stainless Steel

Corrosion Inhibition Behavior of Brass Tube by Sodium Diethyldithiocarbamate

Inhibition of sodium dodecyl benzene sulfonate for stainless steel

Performance of a Composite Inhibitor on Mild Steel in NaCl Solution: Imidazoline, Sodium Molybdate, and Sodium Dodecylbenzenesulfonate

Inhibition of Corrosion of Mild Steel by Sodium N,n-Diethyl Dithiocarbamate in Hydrochloric Acid Solution

Corrosion Inhibition of Sodium Dodecyl Benzene Sulfonate to Stainless Steel

Inhibition Effect of Silicate and Molybdate on the Corrosion of SS 316 in Neutral Corrosive Solution at High Temperature

Corrosion inhibition performance of synergistic inhibitors on Q235 steel in methanol/formic acid medium

Corrosion Inhibition Control of Ferritic Stainless Steel in Hydrochloric Acid Electrolytes

Corrosion Inhibition Performance of Composite Inhibitors for Carbon Steel in Simulated Seawater

Corrosion Inhibition by Sorbitol/Diethylenetriamine Condensation Product for Carbon Steel in 3.5% NaCl Saturated Ca(OH)2 Solution

Sodium Diethyldithiocarbamate As a Corrosion Inhibitor of Cold Rolled Steel in 0.5 M Hydrochloric Acid Solution

Synergistic Effect of 4-Dimethylaminopyridine with Sodium Dodecyl Sulfonate and Potassium Bromide on the Corrosion Inhibition of Mild Steel in HCl Medium: a Collective Experimental and Computational Investigation

INHIBITION BEHAVIOR OF MOLYBDATE INHIBITORS FOR CARBON STEEL IN SEA WATER

Effect of Diamino ( ( 2-( ( 2-Aminoethyl ) Amino ) Ethyl ) Amino ) Methanethiol on the Corrosion Resistance of Carbon Steel in Simulated Concrete Pore Solutions

Inhibitors for the Pitting Corrosion of Stainless Steel in Circulating Cooling Water

Corrosion Inhibition Behavior of Compound Salicyladehyde Schiff Base Inhibitor for Carbon Steel in Seawater

Inhibition Performance of Enhanced-Mo Inhibitor for Carbon Steel in 55% Libr Solution

Inhibition Performance of N,N'-di(2-thiobenzothiazole-3-methyl)-Dodecan Amine

Didecyl Dimethyl Ammonium Chloride As a Highly Efficient Corrosion Inhibitor for Carbon Steel in Hydrochloric Acid Solution

Synthesis, Anti-corrosion Performance and Mechanism Research of Amphoteric Gemini Surfactant(TCDSQ-22) as Corrosion Inhibitor on Stainless Steel