Abstract:This study investigates the relationship between aging temperature on the precipitation behavior and mechanical properties of a gravity cast Al-5.0Mg-3.0Zn-1.0Cu (wt%) alloy. After solution treatment at 470 °C for 24 h, alloys were aged at 120, 150 and 175 °C. Upon analyzing the samples, the alloys displayed different age hardening behaviors due to the variations in aging temperature. An increase in aging temperature not only reduced the peak aging time significantly, but also changed the distribution of precipitates. Numerous GPII zones and T′ precipitates (precursors of T-Mg32(AlZn)49) were homogeneously distributed within matrix at a higher aging temperature and the volume fraction of T′ precipitates increased. Tensile test results for peak-aged samples determined that both yield strength (YS) and ultimate tensile strength (UTS) increased, while elongation (EL) decreased with increasing temperature. The increase in the YS can be attributed to the higher volume fraction of T′ precipitates caused by the higher aging temperature. Moreover, the impact toughness decreased (due to a continuous decrease in EL) as the aging temperature increased. By adjusting aging temperature from 120 to 175 °C, YS increased from 377 to 451 MPa, while EL decreased from 13.8% to 5.2%. After peak aging treatment at 150 °C, the alloy appears to possess optimal mechanical properties with YS, UTS, EL and toughness being 441 MPa, 496 MPa, 9.6%, and 8.1 J/cm2, respectively. These finding suggest that there are many potential advantageous applications for this alloy within automobile components requiring high strength and toughness.

Promoted Aging Precipitation Behavior of Tc4/Gz151k Magnesium Matrix Composites

Processing, microstructure and ageing behavior of in-situ submicron TiB2 particles reinforced AZ91 Mg matrix composites

Precipitation Behavior and Mechanical Performances of A356.2 Alloy Treated by Al–Sr–La Composite Refinement-Modification Agent

Investigation on peripheral coarse grains and precipitation behavior of in-situ TiB2/Al–Cu–Mg composites with various Mg contents

Microstructure Evolution and Mechanical Properties of As-Cast and As-Compressed ZM6 Magnesium Alloys during the Two-Stage Aging Treatment Process

Tuning the microstructure features of in-situ nano TiB2/Al-Cu-Mg composites to enhance mechanical properties

Effect of aging hardening on in situ synthesis magnesium matrix composites

Effect of in-situ (TiC-TiB2) reinforcement on aging and mechanical behavior of AZ91 magnesium matrix composite

Effects of aging treatment on the precipitation behaviors and mechanical properties of Al-5.0Mg-3.0Zn-1.0Cu cast alloys

Age-hardening Behavior for Discontinuously Reinforced MB15 Magnesium Matrix Composites by Powder Metallurgy

Microstructure Evolution and Mechanical Properties of High Performance Mg–10Gd–2Y–0·5Zn–0·3Zr Alloy During Heat Treatments

Study on Microstructure and Mechanical Properties of TC4/AZ31 Magnesium Matrix Nanocomposites

Effects of Mg/Zn ratio and pre-aging on microstructure and mechanical properties of Al–Mg–Zn–Cu alloys

Effect of twin assisted precipitation on the microstructure and mechanical properties of gradient structure Mg-Gd-Zn-Zr alloy

Effect of Ti6Al4V reinforcement particles on the mechanical, wear, and corrosion properties of AZ91D magnesium matrix composites

Two-stage aging treatment to accelerate aging kinetics without impairing strength in B4C/7A04Al composite

The Effect of Graphene Nanoplatelets on the Aging Precipitation Behavior and Mechanical Properties of Magnesium Matrix Composite

Influence of Ti-6Al-4V particles on the interfacial microstructure and strength-ductility synergetic mechanism of AZ91 magnesium alloy

Effect of aging treatment on microstructure and mechanical properties of Al matrix composite reinforced by in-situ intragranular Al 2 O 3

Microstructure modification and precipitation strengthening for Mg–6Zn–1Mn–4Sn–0.5Ca through extrusion and aging treatment

Effect of Heat Treatment on Microstructure and Mechanical Properties of Squeeze Cast n SiCp/AZ91D Magnesium Matrix Composites