High Strength and Ductility of Cast Mg-9Gd-1.5Y-0.8Zn-0.3Zr Alloy Achieved by Microstructural Regulation

Daiyi Deng,Renju Cheng,Zhihua Dong,Bin Jiang,Mingbo Yang,Haijun Wang,Chuntang Yu,Yanlong Ma,Fusheng Pan
DOI: https://doi.org/10.1016/j.pnsc.2023.12.001
2023-01-01
Abstract:This work reports a high strength and ductility as-casted Mg-9Gd-1.5Y-0.8Zn-0.3Zr (wt.%) alloy by using the optimized heat treatment of a lower solid-solution temperature of 480 degrees C and then aging at 200 degrees C for 48 h with the ultimate tensile strength and yield strength reached 374(+/- 2.0) MPa and 270.5(+/- 5.5) MPa, respectively, whilst a high elongation of 10.1(+/- 1.3) % was achieved. The high strength and ductility are found to emerged primarily from the synergic influence of long period stacking ordered (LPSO) phases and the nano-beta ' precipitates: at lower temperature of 480 degrees C the alloy preserved a large number of block and lamellar 14H-LPSO phases at the grain boundaries and the smallest size of beta ' precipitates led to a better ductility and higher strength. While at higher temperatures solid-solution treatment of 500 degrees C and 520 degrees C, the strength and ductility declined slightly due to the lamellar or filminess LPSO formed in the grains, and especially the precipitation of cubic-shaped RE-enriched phases and rod-like Zn-Zr compounds. Particularly when the solid solution temperature reached as high as 520 degrees C, the strength was significantly reduced due to the increase of the cubic-shaped RE-enriched phases. We suppose that the efficiency of the morphology and position of LPSO phases on the ductility strengthening of the alloy is block and lamellar LPSO phases in the grain boundaries > lamellar or filminess LPSO phases in the grains.
What problem does this paper attempt to address?