Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

Quantitative Analysis of Micro-Crack Formation in Machining of Nickel-Based Cast Superalloy Through In-Situ Imaging Technique

In-situ Observation of Crack Initiation and Propagation in Ni-based Superalloy with Film Cooling Holes During Tensile Test

Effects of Cutting Edge Radius on Surface Integrity in Machining of Nickel-Based Cast Superalloy: an in Situ Imaging Approach

Quantitative Study of High-Frequency Fatigue Hole-Edge Stresses in Nickel-Based Single-Crystal Superalloy

Fatigue Crack Initiation and Propagation Behavior of Nickel-Based Single Crystal DD6 under Different Drilling Processes

Study on milling material removal mechanism and surface integrity of nickel-based single crystal superalloy DD5

Grinding subsurface damage mechanism of nickel-based single crystal superalloy based on stress-strain

Grinding surface and subsurface stress load of nickel-based single crystal superalloy DD5

Microscopic Study on the Mechanism of Tool Bond Wear in Cutting Ni–Fe-Cr-Co–Cu Series Nickel-Base Superalloy

Understanding Tool Cutting-Edge Microstructure and Deformation Mechanism Induced by Adhesive Wear in the Turning of Nickel-Based Superalloys

Finite Element and Experimental Analysis of Grain Refinement Caused by Dynamic Recrystallization During High-Speed Cutting of Nickel-Based Superalloys

Experimental Study on Micro-Grinding Force and Subsurface Microstructure of Nickel-Based Single Crystal Superalloy in Micro Grinding

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

Experimental Study of Micro-Milling Mechanism and Surface Quality of a Nickel-Based Single Crystal Superalloy

A FEM Study on Chip Formation in Orthogonal Turning Nickel-Based Superalloy GH80A

Experimental and numerical investigation of Inconel 718 machining with worn tools

Mechanical Properties and Microstructure Evolution During Dynamic Compression and Cutting of Nickel-Based Superalloys

Multi-Dimensional Revealing the Influence Mechanism of the δ Phase on the Tensile Fracture Behavior of a Nickel-Based Superalloy on the Mesoscopic Scale

Multi-scale modeling reveals microstructural and mechanical evolution in GH4169 and DD5 nickel-based superalloys during grinding

Microstructural insights into fatigue short crack propagation resistance and rate fluctuation in a Ni-based superalloy manufactured by Laser powder bed fusion

Analysis of tool wear and cutting characteristics in milling of powder metallurgy nickel-based superalloy by various coatings