Mechanisms for optimizing the dielectric properties of spinel Li₁₀ZnTi₁₃O₃₂ ceramics by Na<SUP>+</SUP> doping

Haotian Liu,Kui Liu,Da Huang,Qin Yu,Cheng Liu,Jie Li,Yulong Liao,Dainan Zhang,Huaiwu Zhang

DOI: https://doi.org/10.1016/j.ceramint.2024.01.164

IF: 5.532

2024-01-01

Ceramics International

Abstract:Herein, the dielectric properties of Na (+) doped Li10ZnTi13O32 ceramics were investigated by first-principles computational prediction and combined with the solid-phase reaction method. Li9.88Na0.12ZnTi13O32 obtained the best dielectric properties by sintering at 1050 degrees C for 4 h: epsilon(r) = 30.01, Q x f = 90,879 GHz (@7.8 GHz), tau(f) = 3.93 ppm/degrees C. In terms of extrinsic factors, the optimization of the densification, the creation of the second phase TiO2, and the increase of the grain size resulted in better dielectric properties. Intrinsic factors indicate that the weakening of the damping behavior and the increase in the electron cloud density lead to a decrease in the dielectric loss. The increase in ion polarisation and the blue shift of the Raman wavenumber lead to a gradual increase in epsilon(r). The temperature stability is optimized depending on the TiO2 content. The optimized Li9.88Na0.12ZnTi13O32 ceramics have unlimited applications in microwave communications.