Abstract:Nano alpha-aluminum fluorides with high surface area were synthesized by a simple ethylene glycol mediated solgel technique using dilute aq. HF as the F source, and their performances were investigated for gas-phase dehydrofluorination of 1,1,1,2-tetrafluoroethane at relatively low reaction temperature (400 C). Aluminum precursor was crucial for the phase composition, textural and acidic properties of the resulting fluoride. Commercially low-cost and available inorganic Al was firstly used as precursor for synthesis of aluminum fluorides via the solgel route, and the as-prepared alpha-AlF3 possessed high surface area (up to 170 m(2) g(-1)) and strong surface acidities even after thermal treatment of 400 C. The presence of sulfate ions suppressed the crystallization of aluminum fluoride during calcination when Al-2(SO4)(3) was used as precursor, leading to an amorphous phase for as-prepared AlF3. Aluminum fluorides with beta and pyrochlore phase were prepared using aluminum isopropoxide and aluminum diacetate hydroxide, respectively, as precursors. Based on the results of IR, XRD and element analysis, it is concluded that the formation of Al-glycolates during the solgel process can effectively reduce the hydrolysis of precursor and suppress particle agglomeration, thus leading to dominant formation of nano aluminum fluorides. The residual O derived from minor hydrolysis can resist sintering under high-temperature treatment, which is a key factor to improve the thermostability of as-prepared aluminum fluoride. Due to their large Lewis acidic amounts, the alpha-AlF3 derived from AlOOH and Al2O3 exhibited remarkably high catalytic activity with CF3CH2F conversion of 24%28% and CF2=CHF selectivity above 98%, which were far higher than that of AlF3 prepared by traditional methods. (C) 2016 Elsevier B.V. All rights reserved.

Highly Efficient C–F Bond Cleavage to Access Esters over Robust Silicon-Aluminum Phosphate Catalyst

A Mechanistic Study of the Hydrolysis of Tetrafluoromethane on Γ-Alumina

Single-Atom Pt Catalyst for Effective C–F Bond Activation Via Hydrodefluorination

Evolution of Lewis acidity by mechanochemical and fluorination treatment of silicon carbide as novel catalyst for dehydrofluorination reactions

Catalyst-free Defluorinative Alkylation of Trifluoromethyls

Efficiently nucleophilic trifluoromethylation of aldehydes over MgSO4/ ZrO2 catalyst

Carbodefluorination of fluoroalkyl ketones via a carbene-initiated rearrangement strategy

Defluorinative Esterification and 1,3-Dietherification of (trifluoromethyl)alkenes with Alcohols: Controlled Synthesis of Α-Arylacrylates and 1,3-Diethers

Asymmetric Silver-Catalysed Intermolecular Bromotrifluoromethoxylation of Alkenes with a New Trifluoromethoxylation Reagent

Defluorinative C−O Coupling between Trifluoromethylarenes and Alcohols via Copper Photoredox Catalysis

Dehydrofluorination as a Residue-Free Selective Route to C–C Bond Formation at Metal Surfaces

A robust depolymerization route for polysiloxanes

Oxidative Trifluoromethylation and Trifluoromethylthiolation Reactions Using (Trifluoromethyl)trimethylsilane as a Nucleophilic CF3 Source

Visible-Light-Mediated C− F Bond Cleavage for the Synthesis of Polyfluorinated Compounds

Stabilizing F-Al-O active center via confinement of Al 2 O 3 in SiC framework for conversion of 1,1-difluoroethane greenhouse gas

Sequential C–F Bond Transformation of the Difluoromethylene Unit in Perfluoroalkyl Groups: A Combination of Fine‐Tuned Phenothiazine Photoredox Catalyst and Lewis Acid

A Continuous Flow Process for the Defluorosilylation of HFC-23 and HFO-1234yf

Copper-catalyzed aerobic oxidative trifluoromethylation of H-phosphonates using trimethyl (trifluoromethyl) silane

A Facile Sol-Gel Synthesis of Highly Active Nano Α-Aluminum Fluoride Catalyst for Dehydrofluorination of Hydrofluorocarbons

Confined aluminum fluoride layers derived from the in situ etching of Ti3AlC2 as the robust catalyst for dehydrofluorination reaction

Chemical Strategies for the Cleavage of the C(sp3)−F Bonds in Perfluoroalkyl Groups