Effect Of Al2o3 Particles On Sintering Properties Of Litao3
Yf Zhang,Y Zhou,Dc Jia,Hy Li
DOI: https://doi.org/10.3321/j.issn:1002-185X.2005.z1.148
2005-01-01
Rare Metal Materials and Engineering
Abstract:Pure LiTaO3 and Al(2)O(3)p/LiTaO3 (ALT) ceramic composites (containing 5 vol%, 10 vol%, 15 vol%, 20vol% Al2O3p, respectively) were fabricated by hot pressing in nitrogen atmosphere. When introducing Al2O3 particles, the densities of LiTaO3 based ceramics rise obviously, over 99% for all the ALT ceramic composites. Contrarily, The introduction of LiTaO3p into Al2O3 ceramics could strikingly promotes the densities of the Al2O3 based composites and decreased significantly the sintering temperature of Al2O3 ceramic. It was observed that Al2O3p could coexist with LiTaO3 ceramic matrix in the composite sintered at 1 300 degrees C, which reveals a good chemical compatibility of both phases. Al2O3p disperse homogeneously along LiTaO3 grain boundaries and bond tightly with the matrix, free microcracks in the bulk materials, which revealed that Al2O3 and LiTaO3 had good thermophysical compatibility. Summarily, both Al2O3 and LiTaO3 have good compatibilities in the composite system.