Abstract:Nb3Sn conductors are important candidates for high-field magnets for particle accelerators, and they continue to be widely used for many laboratory and NMR magnets. However, the critical current density, Jc, of present Nb3Sn conductors declines swiftly above 12-15T. State-of-the-art Ta- and Ti-doped strands exhibit upper critical field, Hc2, values of 24-26.5T (4.2K) and do not reach the FCC target Jc, which serves as the present stretch target for Nb3Sn development. As recently demonstrated, to meet this goal requires enhanced vortex pinning but an independent and supplementary approach is to significantly enhance Hc2. In this study, we have arc-melted multiple Nb alloys with added Hf, Zr, Ta and Ti and drawn them successfully into monofilament wires to investigate the possibilities of Hc2 enhancement through alloying. Hc2(T) was measured for all samples in fields up to 16T and some up to 31T. We have found that all alloys show good agreement with the standard Werthamer, Helfand, and Hohenberg (WHH) fitting procedure without the need to adjust the paramagnetic limitation parameter (alpha) and spin-orbit scattering parameter (lambda_so). The evaluation of dHc2/dT near Tc, which is proportional to the electronic specific heat coefficient (gamma) and the normal state resistivity (rho_n), allows a better understanding of the induced disorder introduced by alloying in the A15 phase. So far, we have observed that Hf alloying of pure Nb can enhance Hc2(0) by 3-4T to 28T, while adding just 1 at. %Hf or Zr into a Nb4Ta base alloy can raise Hc2(0) to 31T. Very importantly we find that Hf and Zr raise the alloy recrystallization temperature above the usual A15 reaction temperature range of 650°C-750°C, thus ensuring denser A15 phase nucleation in the Nb alloy grain boundaries, possibly leading to a more homogeneous A15 phase Sn content and refined A15 grain size. The potential for...

Influence of Hf Addition on the Superconducting Properties of Nb3Sn

Effect of Hf Addition to Nb on Nb 3 Sn Grain Morphology Under High Sn Diffusion Driving Force

Influence of Nb Alloying on Nb Recrystallization and the Upper Critical Field of Nb3Sn

Comparative drawability and recrystallization evaluation of Nb4Ta and Nb4Ta1Hf alloys, and the beneficial influence of Hf on developing finer Nb3Sn grain size

Beneficial influence of Hf and Zr additions to Nb4at.%Ta on the vortex pinning of Nb$_{3}$Sn with and without an O source

Effect of Cubic Equiaxed Grains and Its Ti-Stabilizing Performance in Nb3sn Strands

THE EFFECT OF Nb ON SUPERCONDUCTING Tc OF C-15 V2 (Hfzr)

Flux Pinning Effect of Cubic Equiaxed Morphology and Its Ti Stabilizing in Nb3Sn Superconductors

Microstructural Characteristics of Nb–Si Based Ultrahigh Temperature Alloys with B and Hf Additions

Tailoring the magnetic properties and microstructure of NdFeB ribbon alloys by Hf addition

Effect of Nb3Sn Coarse Grains on Critical Current Densities of Internal Tin Nb3Sn Strand

In-depth S/TEM observation of Ti–Hf and Ta–Hf-doped Nb3Sn layers

Ta, Ti and Hf effects on Nb$_3$Sn high-field performance: temperature-dependent dopant occupancy and failure of Kramer extrapolation

Microstructure and Room Temperature Mechanical Properties of Hf and Sn-Doped Nb-20ti-5cr-3al-18si Alloy

Effects of Hf Addition on the Microstructure and Properties of Cu-Sn-P Alloy

A review and prospects for Nb3Sn superconductor development

The Effects of Cu, Nb and Zr Additions on the Permanent Magnetic Properties of Melt-Spun Sm–Fe–Si–C Ribbons

Effects of Hf Addition on the Microstructure, Magnetic Properties and Coercivity Mechanism of Nd-Ce-Fe-B Ribbons Fabricated by Melt-Spinning Technique

Effects of Hf on Phase Structure and Magnetic Performance of Nanocrystalline SmCo7-type Alloy

High-temperature-tolerable superconducting Nb-alloy and its application to Pb- and Cd-free superconducting joints between NbTi and Nb3Sn wires

Enhancement of the Upper Critical Field in the Cubic Laves-phase Superconductor HfV2 by Nb Doping