Abstract:Pristine Y0.5Gd0.5Ba2Cu3O7-δ films and Y0.5Gd0.5Ba2Cu3O7-δ films with additional 1 mol% and 3 mol% BaHfO3 secondary phases were fabricated on a CeO2 layer, and the microstructure and superconducting properties in the liquid helium, hydrogen, and nitrogen temperature regions were compared. BaHfO3 dopants exist in the form of nanorods and cause lengthening of the Y0.5Gd0.5Ba2Cu3O7-δ c-axis lattice and degradation of the texture due to the strain field, which, in turn, reduces the critical temperature and self-field critical current density. The field and temperature dependences of the transport characteristics were investigated in an applied magnetic field normal to the film by up to 9 T. The fitting on the normalized pinning force density shows effective modulation in the flux creep by doping BaHfO3 over a wide temperature range, which is more significant with increasing doping concentrations. The analysis of the pinning contribution weight confirmed enhancement of the strong pinning by the BaHfO3 nanorods over the entire temperature range, which further explained the weakened attenuation of the current transport capacity in the BaHfO3-doped films with an increasing field. The angular dependence measurement at 77.3 K showed that the BaHfO3 nanorods along the c-axis effectively consolidated the pinning ability approaching the main growth orientation, which leads to improved in-field Jc anisotropy.

Enhancement of the Upper Critical Field in the Cubic Laves-phase Superconductor HfV2 by Nb Doping

THE EFFECT OF Nb ON SUPERCONDUCTING Tc OF C-15 V2 (Hfzr)

Superconductivity Induced by La Doping in Sr 1-X La X FBiS 2

High Field Phase Diagram of Cuprates Derived from the Nernst Effect

The Effect of Nb on Phonons of Superconductors C-15v2zr and V2(Hfzr)

Influence of Hf Addition on the Superconducting Properties of Nb3Sn

Evidence That the Upper Critical Field of Nb3Sn is Independent of Whether It is Cubic or Tetragonal

Te Substitution Effect in Low-Dimensional Superconductor NbSe<sub>2-x</sub>Te<sub>x</sub> (x = 0, 0.1, 0.2)

Significant improvement of the lower critical field in Y doped Nb: potential replacement of basic material for the radio-frequency superconducting cavity

Large upper critical fields and strong coupling superconductivity in the medium-entropy alloy (Ti1/3Hf1/3Ta1/3)1-xNbx

Evidence of unconventional superconductivity in the Ni-doped NbB2 system

Effect of Hf Addition on Critical Current Density of (y,eu)ba 2 Cu 3.6 O 7-Δ Thin Films Prepared by Trifluoroacetate Metal Organic Deposition

Upper Critical Fields and Anisotropy of BaFe 1.9 Ni 0.1 As 2 Single Crystals

Nanoscale-SiC doping for enhancing Jc and Hc2 in the Superconducting MgB2

Upper critical fields and anisotropy of Ca1-xLa xFe2As2 single crystals

Upper critical field measurements using pulsed magnetic fields in Bi1.6Pb0.4Sr2Ca2Cu2+xOy (x=0.8, 1.2, 1.6)

Effects of niobium doping on the charge density wave and electronic correlations in the kagome metal Cs(V1-xNbx)3Sb5

Effects of TiC Doping on the Upper Critical Field of MgB2 Superconductors

In-field Performance Comparison and Vortex Pinning Analysis in Depth of Pristine and BaHfO 3 -Doped Y 0.5 Gd 0.5 Ba 2 Cu 3 O 7- Δ Films in Different Temperature Regions

Superconductivity in Cubic A15-type V–Nb–Mo–Ir–Pt High-Entropy Alloys

Enhancement of the upper critical field in disordered nanocrystalline MgB2 bulks