Structure and Magnetic Properties of TbFe11−xMnxTi Compounds
Shi-Qiang Yang,Chun-Lan Zhang,Ping-Hua Lin,Luo-Xing Li
DOI: https://doi.org/10.1016/j.jallcom.2008.05.051
IF: 6.2
2009-01-01
Journal of Alloys and Compounds
Abstract:The effects of Mn partial substitution for Fe in TbFe11Ti on the structure and magnetic properties were investigated. TbFe11−xMnxTi samples (x=1.0, 2.0, 3.0, 4.0, 5.0) were prepared by means of arc-melting and subsequent vacuum annealing. The structure and magnetic properties of TbFe11−xMnxTi compounds were investigated by X-ray powder diffraction and magnetic properties measurements. The following conclusions were obtained: all the TbFe11−xMnxTi compounds studied crystallize in the ThMn12-type structure; the unit-cell volume increases monotonically with increasing Mn concentration; a compensation temperature was observed in the magnetization–temperature curve of TbFe7Mn4Ti and TbFe6Mn5Ti compounds. With increasing Mn concentration, the saturation magnetization at 4.4K decreases to zero, and then increases again, the magnetic moments of the transition-metal sublattice of TbFe11−xMnxTi compounds decrease monotonically.