Structural and Magnetic Properties of (nd1−xtbx)3fe27.31ti1.69 (0⩽x⩽1.0) Compounds
WQ Wang,JL Wang,BD Liu,WX Li,GH Wu,HM Jin,FM Yang,FR de Boer
DOI: https://doi.org/10.1016/s0921-4526(02)01106-7
2002-01-01
Abstract:The structural and magnetic properties of (Nd1-xTbx)(3)Fe27.31Ti1.69 compounds have been investigated by means of X-ray diffraction and magnetic measurements. It is found that all compounds with x = 0-1.0 retain the Nd-3(Fe,Ti)(29)- type of structure and space group A(2/m). Substitution of Tb for Nd leads to a decrease of the lattice constants and the unit-cell volume, reflecting the lanthanide contraction. With increasing Tb content, the Curie temperature T-C increases slightly, while the saturation magnetization M-s, decreases monotonically. The latter can be described in terms of a simple dilution model. At room temperature, the easy magnetization direction of the (Nd1-xTbx)(3)Fe27.31Ti1.69 compounds depends on the Tb content x and changes from the [40-2] direction for x = 0 to the [040] direction for x = 1.0. As the temperature decreases, a spin-reorientation transition is observed at 233 K in the compound Nd3Fe27.31Ti1.69, whereas no spin reorientation is observed in the compounds in which Tb has been substituted for Nd. The anisotropy field B-a at room temperature increases with increasing Tb content from 3.0 T for x = 0 to 5.2 T for x = 1.0. At low temperatures, a first-order magnetization process (FOMP) (of type-II) is observed in Tb3Fe27.31Ti1.69. The critical field B-cr of the FOMP decreases monotonically with increasing temperature. (C) 2002 Elsevier Science B.V. All rights reserved.