Preparation and Electrochemical Performances of High Voltage Nanosized Al_2O_3 Coating LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2

Meng Huanping,Xiayin Yao,Jingbo Yin,Bingxin Huang,Xiao-Xiong Xu

2015-01-01

Abstract:A layer of nano Al_2O_3 was coated on the surface of LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 particles by sol-gel method, so the cycle performance and rate capability of LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 at a high cut-off voltage are enhanced. The structure and morphology of the materials were characterized by XRD, SEM and TEM. The electrochemical performances of the high voltage cathodes were galvanostatically evaluated. The results show that the structure of the materials does not change after coating. The optimized coating content of Al_2O_3 is 2.0%, corresponding to the layer of 20-30 nm. The electrochemical performances of LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 cathode materials are obviously improved by the Al_2O_3 layer. At the range of 2.8-4.5 V, the first discharge specific capacity of uncoated LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 materials is 175 mAh/g at 0.2 C, and the capacity retention after 50 cycles is 91.8%. At the same charge-discharge conditions, the first specific discharge capacity of coated LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 materials increases to 181 mAh/g, and the capacity retention after 50 cycles still reaches 97.4%. Even at 5 C, the discharge specific capacity of coated LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 materials is 152 mAh/g. The coated LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 materials exhibit huge potential in the lithium ion batteries with high energy density and long cycle life.