Abstract:Here, we report the structural, optical, magnetic, and dielectric properties of La0.67Sr0.33Mn1-x-yZnxCoyO3 manganite with various x and y values (0.025 < x + y < 0.20). The pure and co-doped samples are called S1, S2, S3, S4, and S5, with (x + y) = 0.00, 0.025, 0.05, 0.10, and 0.20, respectively. The XRD confirmed a monoclinic structure for all the samples, such that the unit cell volume and the size of the crystallite and grain were generally decreased by increasing the co-doping content (x + y). The opposite was true for the behaviors of the porosity, the Debye temperature, and the elastic modulus. The energy gap Eg was 3.85 eV for S1, but it decreased to 3.82, 3.75, and 3.65 eV for S2, S5, and S3. Meanwhile, it increased and went to its maximum value of 3.95 eV for S4. The values of the single and dispersion energies (Eo, Ed) were 9.55 and 41.88 eV for S1, but they were decreased by co-doping. The samples exhibited paramagnetic behaviors at 300 K, but they showed ferromagnetic behaviors at 10 K. For both temperatures, the saturated magnetizations (Ms) were increased by increasing the co-doping content and they reached their maximum values of 1.27 and 15.08 (emu/g) for S4. At 300 K, the co-doping changed the magnetic material from hard to soft, but it changed from soft to hard at 10 K. In field cooling (FC), the samples showed diamagnetic regime behavior (M < 0) below 80 K, but this behavior was completely absent for zero field cooling (ZFC). In parallel, co-doping of up to 0.10 (S4) decreased the dielectric constant, AC conductivity, and effective capacitance, whereas the electric modulus, impedance, and bulk resistance were increased. The analysis of the electric modulus showed the presence of relaxation peaks for all the samples. These outcomes show a good correlation between the different properties and indicate that co-doping of up to 0.10 of Zn and Co in place of Mn in La:113 compounds is beneficial for elastic deformation, optoelectronics, Li-batteries, and spintronic devices.

Slight La Doping Induced Ferromagnetic Clusters in Layeredla3−3xsr1+3xmn

Enhanced Room Temperature Magnetoresistance and Cluster Spin Glass Behavior in Mo Doping La0.67Sr0.33MnO3

Effect of Substitution of Magnetic Metal Ions on Magnetic and Magnetoresistance Properties in LaSr<sub>2</sub>Mn<sub>2</sub>O<sub>7</sub>

Mixed Magnetic Exchange Interactions and Ferromagnetic Diffuse Phase Transition of La1−xMnO3+δ Manganites

Origin of magnetic anisotropy in $La_{(1\-x)}Sr_{x}MnO_{3}$

Charge Doping Effects on Magnetic Properties of Single-Crystal La1−xSrx(Cr0.2Mn0.2

The Magnetotransport Properties of LaMn1−xCrxO3 Manganites

Band filling effect on polaron localization in La$_{1-x}($Ca$_y$Sr$_{1-y}$)$_{x}$MnO$_3$ manganites

Effect of Mn Doping and Charge Transfer on LaTi1-xMnxO3.

A-site Disorder Induces Magnetoresistance in Y and Sr Co-Doped La2/3−xYxCa1/3−ySryMnO3

Magneto-transport and specific heat behavior of Cd-doped LaCaMnO

Effect of electron doping on the magnetic correlations in the bilayered brownmillerite compound Ca_{2.5-x}La_{x}Sr_{0.5}GaMn_{2}O_{8}: a neutron diffraction study

Antiferromagnetic to ferromagnetic phase transition as a transition to partial ordered spins. Application to $La_{1-x}Ca_xMnO_3$ in the doping range $x\geq 0.50$

Competing Magnetic Interaction In Co Doped La0.7sr0.3mno3

Competing Magnetic Interactions in Co-Doped La<sub>0.7</sub>Sr<sub>0.3</sub>MnO<sub>3</sub>

Structural, magnetic, magnetocaloric, investigations on La0.8−xKxSr0.2Mn0.95Ni0.05O3 (x = 0.05, 0.10 and 0.15) at room temperature

Influence of Sr substitution on structural, magnetic and magnetocaloric properties in La0.67Ca0.33−xSrxMn0.98Ni0.02O3 manganites

The Magnetic and Transport Properties of Fe Doped La0.5ca0.5mno3

MAGNETO-ELECTRIC PROPERTIES OF MONOVALENT Na ELEMENT DOPING AT A SITE OF LaMnO_3

Structural, Optical, Magnetic, and Dielectric Investigations of Pure and Co-Doped La0.67Sr0.33Mn1-x-yZnxCoyO3 Manganites with (0.00 < x + y < 0.20)

Magnetic and Transport Properties of Cobalt Doped La0.7Sr0.3MnO3