Abstract:La0.8Na0.2-x □ x MnO3 (0.00 ≤ x ≤ 0.15) manganites were successfully synthesized using the solid-state route. X-ray diffraction was performed to check the samples' purity and phase structure. Scanning electron microscopy analysis reveals a decrease in the average grain size with an increase in the deficiency amount. Analysis of the temperature dependence of magnetization proved the presence of ferromagnetic-paramagnetic transition in all the studied samples. The magnetization derivative (d2 M/dT 2) curves demonstrated a decrease in the transition temperature with an increase in the deficiency amount. Such experimental observations can be correlated with bandwidth evolution, which affected double-exchange interactions. It can be equally accounted for by the average grain size decrease. In this regard, the experimental measurements of effective paramagnetic moments revealed the existence of ferromagnetic correlations within the paramagnetic phase. Notably, different electrical findings were addressed. Indeed, the frequency dependence of electrical conductivity displayed the coexistence of two frequency slopes reflecting the presence of Jonscher's double power law for all the studied samples. A significant decrease in conductivity values was observed when the deficiency amount increased. This experimental observation could be assigned to the decrease in the grain size (conductor region). Such assumption was confirmed by the evolution of the grain boundary resistance with deficiency level. Indeed, a significant mounting in the grain boundary resistance values was obtained presenting the increase of the resistive region for x = 0.15. It is worth noting that the Curie temperature for the x = 0.10 sample was found to be close to room temperature (T C = 297 K). These findings make the La0.8Na0.1□0.1MnO3 compound a powerful candidate for many technological applications.

MAGNETO-ELECTRIC PROPERTIES OF MONOVALENT Na ELEMENT DOPING AT A SITE OF LaMnO_3

Structural, Magnetic, and Electrical Properties of LaMnO3 Doped with Na by Microwave-Assisted Synthesis Method

HE ELECTICAL-RANSPORT PROPERTIES OF THE MO-DOPING La0.7Ca0.2Ba0.1Mn1-xMoxO3

Enhanced Room Temperature Magnetoresistance and Cluster Spin Glass Behavior in Mo Doping La0.67Sr0.33MnO3

Effect of Mn Doping and Charge Transfer on LaTi1-xMnxO3.

Theoretical Studies of Electronic and Magnetic Properties of Mn-Site-Doped Perovskites LaMn1-xNixO3

The Magnetotransport Properties of LaMn1−xCrxO3 Manganites

Structural, morphological, magnetic and electrical properties of La0.8Na0.2- x □ x MnO3 (0.00 ≤ x ≤ 0.15) manganites

Effect of Substitution of Magnetic Metal Ions on Magnetic and Magnetoresistance Properties in LaSr<sub>2</sub>Mn<sub>2</sub>O<sub>7</sub>

Magnetic Properties in Α-Mno2 Doped with Alkaline Elements

The Magnetic and Transport Properties of Fe Doped La0.5ca0.5mno3

Study on Structural and Transport Properties of Nonstoichiometric La0.67Sr0.33-x□x MnO3

Singular Behavior Observed in the Low Temperature Electronic Transport and Thermodynamic Properties of Mn Doped Na0.68coo2

Structural, magnetic, magnetocaloric, investigations on La0.8−xKxSr0.2Mn0.95Ni0.05O3 (x = 0.05, 0.10 and 0.15) at room temperature

MAGNETO-ELECTRONIC PROPERTIES AND INFRARED OPTICAL ANALYSIS OF La2/3-xYxCa1/3MnO3

Enhanced low field magnetoresistance in Mn substituted nanocrystalline La0.7Sr0.3Mn0.9M0.1O3

A-site Disorder Induces Magnetoresistance in Y and Sr Co-Doped La2/3−xYxCa1/3−ySryMnO3

The Significant and Temperature-Insensitive Magnetoresistance Observed in Co-doped (la0.7sr0.3)mno3 Thin Films

Mixed Magnetic Exchange Interactions and Ferromagnetic Diffuse Phase Transition of La1−xMnO3+δ Manganites

Effect of Ga and Mn Doping on Structural, Electrical Transport and Magnetic Properties of Na0.75CoO2

Effect of Mn-site Vacancies on the Magnetic Entropy Change and the Curie Temperature of La0.67Ca0.33Mn1−xO3 Perovskite