Abstract:Highly crystalline Fe-Al-EU-1 zeolites were hydrothermally synthesized in a HMBr2-Na2O-Al2O3-SiO2-Fe2O3-H2O system by using hexamethonium bromide (HMBr2) as a template. The physical and chemical properties, and the bonding state of Fe in the zeolite framework for the prepared Fe-Al-EU-1 samples were characterized by a series of techniques including X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric-derivative thermogravimetric (TG-DTG) analysis, N-2 adsorption-desorption, solid-state nuclear magnetic resonance (NMR), UV-visible diffuse reflectance spectroscopy (UV-Vis DRS), and X-ray absorption fine structure (XAFS). The results show that with increasing the mass fraction of Fe in the original sol-gel, the unit cell volume of Fe-Al-EU-1 zeolite inflates; the zeolite doped with Fe causes an increase in its surface area (BET) from 272 to 365 m(2) . g(-1) and a reduced amount of template removal, as well as a decrease in decomposition temperature. Adding Fe ions into sol-gel also leads to lowered zeta potential, easily gathered colloidal particles, and increased shape of zeolite. The UV-Vis spectrum shows that there is a characteristic peak at about 220-250 nm with a sharply increased intensity due to the p-d transition of the bonding electrons from the 2p-orbital of 0 atom to the d-orbital of the four-coordinated Fe atom in the framework. Also at around 373 nm, the coordination bonding of four-coordinated Fe atoms and adjacent Si - O groups leads to a d-d charge transition peak with an energy level splitting and increased peak intensity. The XAFS results show that with the crystallization process going on, the pre-edge absorption peak for 1s -> 3d and main absorption peak for 1s -> 4p change significantly. Four-coordinated structural units of iron species formed from the original sol-gel samples are gradually transformed into a tetrahedral coordinated iron-silicon-oxygen skeleton, in which iron-silicon-oxygen ionic structural unit is also transformed into skeleton iron species with a tetrahedral covalent bonding structure.

SYNTHESIS AND CHARACTERIZATION OF Fe(II)SALEN COMPLEX IN ZEOLITE BETA

SYNTHESIS AND CHARACTERIZATION OF Fe( Ⅱ )SALEN COMPLEX IN ZEOLITE BETA

FeSALEN COMPLEXES ENTRAPPED IN ZEOLITE MCM-22

Synthesis and characterization of Zinc(II) complex with (1R, 2R)-(-)-Diaminocyclohexane-N,N'-bis(3-tert-butyl-5 -(4'-methylbenzoate)- salicylidene)

Synthesis and characterization of MCM-49/ZSM-35 composite zeolites in the hexamethyleneimine and cyclohexamine system

Synthesis, Physicochemical Characterization, and Catalytic Evaluation of Fe<SUP>3+</SUP>-Containing SSZ-70 Zeolite

Study of the Crystal Structure of Oxo-Bridged Binuclear Fe-Iii Complex with Chiral Salen Ligand

Synthesis and characterization of β zeolite from aluminosilicate sol containing fluorion

Synthesis, Reactivity, and Complexation with Fe(0) of a Tight‐bite Bis(N‐heterocyclic silylene)

Synthesis of FER/MFI composite zeolite using isopropylamine as a structure-directing agent

Synthesis and characterization of composite molecular sieves comprising zeolite Beta with MCM-41 structures

Analysis of Fe species in zeolites by UV–VIS–NIR, IR spectra and voltammetry. Effect of preparation, Fe loading and zeolite type

A Facile and Green Method for the Synthesis of SFE Borosilicate Zeolite and Its Heteroatom‐Substituted Analogues with Promising Catalytic Performances

A Novel Method of Secondary Synthesis of Fey Zeolite

Synthesis of FER Zeolite Using 4-(Aminomethyl)pyridine as Structure-directing Agent

Salen-based ionic polymers as efficient heterogeneous catalysts for CO 2 cycloaddition

Highly Mesoporous Single-Crystalline Zeolite Beta Synthesized Using a Nonsurfactant Cationic Polymer As a Dual-Function Template.

Synthesis And Characterization Of A Trinuclear Zinc(Ii) Complex With Schiff Base (1r,2r)-(-)-Diaminocyclohexane-N,N '-Biscarboxyl-Salicylidene)

Designed Synthesis and Crystallization of Fe-Al-EU-1 Zeolites Containing Framework-Iron

Synthesis and Structure of Polymorph B of Zeolite Beta

Advances in the synthesis, characterisation, and mechanistic understanding of active sites in Fe-zeolites for redox catalysts