Effect of Thickness on Structure and Property of Black Microarc Oxidation Coatings Prepared on Different Aluminum Alloys
Lei Liu,Laishi Li,Yusheng Wu,Yuzheng Wang,Wei Zhang,Zebin Bao,Ziping Qiao
DOI: https://doi.org/10.11933/j.issn.1007-9289.20221206001
2023-01-01
China surface engineering
Abstract:Aluminum alloys are widely used because of their low density and remarkable strength; however, they are prone to corrosion and wear. Dyeing microarc oxidation technology has gained widespread attention as an emerging surface treatment method. In this study, black microarc oxide coatings are prepared on the surfaces of three aluminum alloy substrates (7075, 7A04, and 2A12) using the constant-current method. The microstructure, hardness, wear resistance, and corrosion resistance of black microarc oxide coatings on the surfaces of the aluminum alloy substrates are investigated using scanning electron microscopy, X-ray diffraction, microhardness testing, friction wear testing, and electrochemical experiments. The black graphite dye improved the microscopic morphology of the film layer and reduced the micropore sizes. Microcracks are significantly reduced, resulting in increased layer thickness without a significant decrease in density. In addition, the change in the aluminum alloy matrix did not alter the structure of the black microarc oxide coatings. The black microarc oxide coatings are mainly composed of a-Al2O3 and y-Al2O3, with the thickness increasing as y-Al2O3 gradually transformed into a-Al2O3. The thickness of the microarc oxide coatings are significantly influenced the hardness of the coating layer. For the 7075 aluminum alloy, the average hardness of the black ceramic oxide coating with a thickness of 40 mu m is approximately 645 HV, increasing to 731 and 780 HV when the thicknesses of the black microarc oxide coating reached 50 and 60 mu m, respectively. The hardness values increased to 790 and 916 HV when the black coating thicknesses reached 50 and 60 mu m, respectively. For the 2A12 aluminum alloy, the hardness of the 60-mu m-thick black ceramic-oxide coating is significantly higher than those of the 50-and 40-mu m-thick coatings, with maximum and minimum hardness values of 904 and 572 HV, respectively, for the 40-mu m-thick black ceramic-oxide coating. As the coating thickness increased, the dense density of the coating increased significantly. The average porosity rate decreased to 0.8%, the proportion of a-Al2O3 in the coating increased, and the wear resistance increased significantly. Moreover, the frictional factor of the composite coating decreased from 0.6 to 0.3 with the self-lubrication effect of the black ceramic particles, and the frictional curve tended to change more smoothly. The thickness of the black microarc oxidation coating increased from 40 to 60 mu m, and the wear resistance of the black oxide coating on all three aluminum alloy substrates increased significantly. The electrochemical results also show that the corrosion resistance of the three aluminum alloys with black microarc oxide coating thicknesses of 50 and 60 mu m is superior. The polarization curves indicates that the corrosion current density of the 60-mu m-thick black microarc composite coating is two orders of magnitude lower than that of the 40-mu m-thick black microarc oxide coating, and the self-corrosion potential can be increased by 200 mV. The black microarc oxide coatings of the 7A04 and 2A12 aluminum alloys are exhibited improved corrosion resistance, close to the excellent corrosion resistance of the white microarc oxide coating of the 7075 aluminum alloy. The corrosion current density of the 60-mu m-thick black microarc oxide coating is two orders of magnitude lower than that of the 40-mu m-thick coating, and the self-corrosion potential can be increased by 200 mV. The passivation performance is improved, and the corrosion resistance of the coating is increased significantly.