Synthesis, Analysis and Characterization of Bimetallic Oxide NiO@NiCo2O4 Composite Nanoarchitectonics from Metal–organic Framework in Electrode Material

J. Shang

DOI: https://doi.org/10.1007/s00339-023-07257-x

2024-01-01

Abstract:The phenomenon of poor cycle stability can be effectively solved by using metal–organic frameworks (MOFs) as precursor to obtain oxides. In this work, a layered NiO@NiCo2O4 nanocomposite electrodes were designed from bimetallic (Ni/Co) based bimetallic metal–organic framework (Ni/Co-MOF) by simple hydrothermal method followed by subsequent controlled calcination under air atmosphere at various temperatures for the transition process. XRD and FE-SEM studies were substantiating the formation of MOF derived NiO@NiCo2O4 nanocomposite with layered structure. Interestingly, electrochemical studies shows that MOF derived NiO@NiCo2O4 nanocomposite achieved at the calcination temperature at 300 °C and 400 °C demonstrates high specific capacitance of 2461 F/g and 2180 F/g at the current density of 1 A/g, which keeps the precursor Ni/Co-MOF with high specific capacitance peculiarity of 2250 F/g at 2 A/g. In terms of cycle retention rate, the NiO@NiCo2O4 nanocomposite obtained at 400 °C still has a high retention rate of 78