Study on Mechanical Property of Recycled Aggregate Concrete with Different Replacement Ratio under the Combined Action of Sulfate Attack and Freeze-thaw Cycle
Kai ZHANG,Liang-liang CHEN,Ke-bin SHI
DOI: https://doi.org/10.3969/j.issn.1671-1815.2017.07.048
2017-01-01
Abstract:Recycled aggregate concrete is beneficial to the development of urban green and sustainable development.Mechanical property is the basic property of concrete,and it is very important for the application of concrete in the actual engineering.In the northwest of China,the double effects of sulfate attack and freeze-thaw cycle will have adverse effects on the mechanical properties of concrete.Through respectively putting 0％,30％,50％,70％,100％ replacement rate of recycled aggregate concrete was put into 5％ sodium sulfate solution for circulation of 0,40,80,120,160,200,240,280 respectively.Then Inspect of concrete compressive strength,shear strength,splitting tensile strength,dynamic elastic modulus,quality.The result can be listed as follows:after 280 freeze-thaw cycles.The compressive strength loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete compressive strength loss ratio decreased respectively by 36％,30％,21％,13％.The shear strength loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete shear strength loss ratio decreased respectively by 25％,21％,15％,9％.The splitting tensile strength loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete splitting tensile strength loss ratio decreased respectively by 18％,16％,9％,4％.The dynamic elastic modulus loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete dynamic elastic modulus loss ratio decreased respectively by 23％,21％,14％,10％.The mass loss ratio of recycled aggregate concrete with 100％ replacement ratio is the standard,0％,30％,50％,70％ replacement rate of recycled aggregate concrete mass loss ratio decreased respectively by 7％,5％,3％,2％.Finally,combined with the experimental results,the mechanism of the effect of different substitution rates on the mechanical property in recycled aggregate concrete is analyzed in detail.It provides a reference for the application of recycled aggregate concrete in practical engineering.