Abstract:In this work, polydopamine-coated electrospun polystyrene (PS) nanofibrous mats were successfully prepared by simply immersing the PS mats into dopamine alkaline Tris buffer solution for 24 h. The successful growth of polydopamine (Pdop) was confirmed with X-ray photoelectron spectroscopy (XPS). The thickness of the Pdop layer was about 20 nm observed by transmission electron microscope (TEM). The wetting behavior was changed tremendously into superhydrophilicity. Combining the unique characteristics of Pdop as active secondary reaction sites and electrospun mat as a flexible porous support, this hierarchically structured nanofibrous mat can serve as a useful platform for developing porous functional membranes. As demonstrated, oil/water separation and molecule gating membranes were fabricated by using the Michael reaction of Pdop coating with undecanethiol (UT) or 11-mercaptoundecanoic acid (MUA), respectively. As an oil/water separation membrane, the long alkyl chains of UT anchored on the membrane surface increased the contact angle (CA) of water distinctly, and water was blockaded completely while oil smoothly passed through the membrane. Similarly, a molecule gating membrane was constructed based on the pH-induced deprotonation of the carboxyl group of MUA, and its permeation selectivity was confirmed by cyclic voltammetry (CV) with an electrochemical probe. Moreover, the reductive property of the Pdop coating was also utilized to facilely introduce various metal nanoparticles into membrane systems for potential applications, for example, a silver nanoparticle-decorated membrane can be used as an effective antibacterial film as confirmed by the modified Kirby-Bauer method. All performed experiments demonstrate that polydopamine-coated nanofibrous mats can serve as a versatile platform for producing porous functional membranes.

Templated Nanostructured PS-b-PEO Nanotubes Part B Polymer Physics

Templated Nanostructured PS‐b‐PEO Nanotubes

Amorphous Carbon Nanotubes With Tunable Properties Via Template Wetting

Wettability Transition Induced Transformation and Entrapment of Polymer Nanostructures in Cylindrical Nanopores

Abstract Submitted for the MAR12 Meeting of The American Physical Society Sub-nm porous membrane based on cyclic peptide nanotubes1

Fabrication of Patterned Polystyrene Nanotube Arrays in an Anodic Aluminum Oxide Template by Photolithography and the Multiwetting Mechanism

Individual Alumina Nanotubes Coaxially Wrapping Carbon Nanotubes and Nanowires

Tubular Polymer Nanoobjects with a Crosslinked Shell and Inward‐Grafted Polymer Brushes

Synthesis of PNIPAM-co-MBAA copolymer nanotubes with composite control.

Morphologies and Optical Properties of Poly (2-Methoxy-5-ethoxy-p-phenylene) Nanoribril Arrays

General Syntheses of Nanotubes Induced by Block Copolymer Self-Assembly.

Fabrication of Ordered Arrays of Polymethylmethacrylate Nanotube Using Porous Anodic Alumina As a Template

Fabrication and Characterization of CdS Nanotube Arrays in Porous Anodic Aluminum Oxide Templates

Subnanometer porous thin films by the co-assembly of nanotube subunits and block copolymers.

Synthesis of Thermosensitive Pnipam-Co-Mbaa Nanotubes by Atom Transfer Radical Polymerization Within A Porous Membrane

Perylene Nanotubes Fabricated by the Template Method.

Nanoporous nonwoven fibril-like morphology by cooperative self-assembly of poly(ethylene oxide)-block-poly(ethyl acrylate)-block-polystyrene and phenolic resin

Hierarchically structured anatase nanotubes and membranes

Uniform fiber-like polymeric micelles of controlled length containing a photo-cleavable core: Versatile templates toward functional nanotubes

Conductive Polypyrrole and Poly(allylamine Hydrochloride) Nanotubes Fabricated with Layer‐by‐Layer Assembly

Polydopamine-Coated Nanofibrous Mats As A Versatile Platform for Producing Porous Functional Membranes