Preparation and Properties of Liquid Y, Nb-codoped BaTiO3-based PTC Ceramics
DING Shi-wen,PAN Bin,CHUAI Yan-ming,JIA Guang
DOI: https://doi.org/10.16553/j.cnki.issn1000-985x.2011.04.031
2011-01-01
Abstract:A series of nano-Ba0.92-xSr0.08YxTi0.9996-yNbyMn0.0004O3-based PTCR powders were synthesized via solid-state reaction at low temperature using Ba(OH)2·8H2O,Sr(OH)2·8H2O,TiCl4,NbCl5,YCl3 and Mn(Ac)2 as raw materials.In this paper,the Y3+ and Nd5+ donors were firstly codoped into the host lattice in their ionic form.XRD patterns demonstrated that the compounds were mutually miscible in the solid solutions.TEM iamge showed that the as-obtained powder was composed of uniform spherical particles with an average particle size of 60 nm in diameter.The PTC measurements indicated that the room temperature resistance could decrease and the resistance jump could increase by adjusting the doping concentrations of Y and Nb.It was found that the room temperature resistance is near 17.6 Ω,temperature coefficient of resistance(α) is 18.6%/℃,and the ratio of Rmax/Rmin is 6.5×104 when the doping concentrations of Y,Nb and Mn were 0.2 mol%,0.18 mol%,and 0.04 mol%,respectively.Furthermore,the sintering conditions of the PTCR materials were investigated in detail.