Effects of Calcium-Containing Electrolytes on Property of Anodic Coatings Obtained by Micro Arc Oxidation on Mg-1.0Ca Alloys

Xiaoguang Xie

2013-01-01

Abstract:Four kinds of calcium salts were separately added into a base solution of 6 g/L NaOH and 15 g/L sodium phytate,and their influences on the property of anodic coatings formed on Mg-1.0Ca alloys were investigated.The surface morphologies,chemical compositions and structures were characterized by scanning electron microscopy(SEM),energy dispersive spectroscopy(EDS) and X-ray diffractometry(XRD).The dropping test and potentiodynamic polarization tests were applied to evaluate the corrosion degradation rate of anodic coatings.The results demonstrate that CaCO3 can slightly increase the calcium content.The coating thickness increases from 3.4 μm to 8.8 μm and the coating porous uniformity of anodic coatings is obviously improved.The dropping test and potentiodynamic polarization curve analysis shows that CaCO3 can significantly improve corrosion resistance of the anodic coatings.The drop time is extended from 75 s to 116 s,and the self-corrosion current density is reduced from 3.898 μA/cm2to 1.473 μA/cm2,while the corrosion potential is improved from 1.538 V to 1.465 V.