Photoluminescence of Eu{sup 3+}-, Tb{sup 3+}-, Dy{sup 3+}- and Tm{sup 3+}-Doped Transparent GeO{sub 2}-Tio{sub 2}-K{sub 2}O Glass Ceramics

G. Lakshminarayana,Jianrong Qiu,Mikhail G. Brik

DOI: https://doi.org/10.1088/0953-8984/20/33/335106;

2008-01-01

Journal of Physics Condensed Matter

Abstract:In this paper, we present the photoluminescence properties of Eu{sup 3+}-, Tb{sup 3+}-, Dy{sup 3+}- and Tm{sup 3+}-doped potassium-titanium-germanate glasses and glass ceramics. Following the x-ray diffraction measurement, the glass structure was established. Compared to Eu{sup 3+}-, Tb{sup 3+}-, Dy{sup 3+}- and Tm{sup 3+}-doped glasses, their respective glass ceramics show stronger emissions due to the presence of the K{sub 2}TiGe{sub 3}O{sub 9} crystalline phase. For Eu{sup 3+}-doped glass and glass ceramics, five emission bands centered at 578 nm ({sup 5}D{sub 0} {yields} {sup 7}F{sub 0}), 592 nm ({sup 5}D{sub 0} {yields} {sup 7}F{sub 1}), 614 nm ({sup 5}D{sub 0} {yields} {sup 7}F{sub 2}), 653 nm ({sup 5}D{sub 0} {yields} {sup 7}F{sub 3}) and 702 nm ({sup 5}D{sub 0} {yields} {sup 7}F{sub 4}) have been observed with 394 nm ({sup 5}D{sub 0} {yields} {sup 7}L{sub 6}) excitation wavelength. Of them, 614 nm ({sup 5}D{sub 0} {yields} {sup 7}F{sub 2}) has shown a bright reddish-orange emission. For Tb{sup 3+}-doped glass and glass ceramic, four emission bands centered at 490 nm ({sup 5}D{sub 4} {yields} {sup 7}F{sub 6}), 549 nm ({sup 5}D{sub 4} {yields} {sup 7}F{sub 5}), 586 nm ({sup 5}D{sub 4} {yields} {sup 7}F{sub 4}) and 621 nm (5{sup D}{sub 4} {yields} {sup 7}F{sub 3}) have been observed with an excitation at 378 nm ({sup 3}F{sub 6} {yields} {sup 5}G{sub 6}) wavelength. Of them, 549 nm ({sup 5}D{sub 4} {yields} {sup 7}F{sub 5}) has shown a bright green emission. With regard to Dy{sup 3+}:glass and glass ceramic, a blue emission band centered at 485 nm ({sup 4}F{sub 9/2} {yields} {sup 6}H{sub 15/2}) and a bright fluorescent yellow emission at 576 nm ({sup 4}F{sub 9/2} {yields} {sup 6}H{sub 13/2}) have been observed, apart from ({sup 4}F{sub 9/2} {yields} {sup 6}H{sub 11/2}) (665 nm) emission transition with an excitation at 387 nm ({sup 6}H{sub 15/2} {yields} {sup 4}I{sub 13/2}), {sup 4}F{sub 7/2}) wavelength. Emission bands of {sup 1}G{sub 4} {yields} {sup 3}F{sub 4} (650 nm) and {sup 3}F{sub 3} {yields} {sup 3}H{sub 6} (700 nm) transitions for the Tm{sup 3+}:glass and glass ceramic, with excitation at {sup 3}H{sub 6} {yields} {sup 1}G{sub 4} (468 nm), have been observed. The stimulated emission cross sections of all the emission bands of Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+} and Tm{sup 3+}:glasses and glass ceramics have been computed based on their measured {delta}{lambda} (FWHM) and lifetimes ({tau}{sub m})