Abstract:Nano-scale nickel oxide materials were prepared by solvothermal method using nickel acetylacetonate, oleic acid and oleylamine as raw materials, octadecene as solvent and polyvinylpyrrolidone as surfactant. The effects of the ratio of reactants ratio, insulation time, surfactant and the mass of oleylamine on the microstructure, particle size, morphology, optics and catalytic properties of the product were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM), ultraviolet-visible spectroscopy (UV-Vis) spectral analysis, and Tafel test. The specific experimental operations were: the oleic acid (OA) and 1-octadecene (ODE) was added into four flasks (500 mL) with heating and stirring. Nickel acetylacetonate was added when the temperature raise to 50 degrees C, then continuously stirring for 60 minutes at 120 degrees C before a certain amount of oleylamine (OAm) was added to the reaction system. The mixed solution was poured into the inner liner of the high temperature reactor. The reactor was covered and transferred to the electro-thermostatic blast oven for a period of time and then cooled to room temperature. The main research results were obtained: (1) The boundary of the original particles became smoothed after sintering, and the spherical particles become flake-shaped which might be attributed to the residual organic covering so the size of nickel oxide nanoparticles changed from the original 40 similar to 45 nm to 30 similar to 40 nm. (2) With the addition of PVP, the content of NiO phase increased and the particle size was controlled within 40 similar to 45 nm. The UV-Vis test showed that NiO belonged to direct band gap and the band gap width was 3.5 similar to 3.7 eV. (3) The Tafel analysis showed that the best catalytic activity with exchange current density J(0) was 1.23x10(-2) mA,cm(-2), where pure NiO could be obtained when the reactant ratio of n[Ni(acac)(2)] : n(OA)-1: 2, the additive PVP mass fraction was of 1.66%, the amount of oleylamine was of 30 mmol, and the temperature was of 200 degrees C for 8 h.

Microwave Hydrothermal Synthesis and Characterization of Microballoon Sphere of Nickel Oxide

The Synthesis of Novel NiO Microsphere Architectures with Electrochemical Behavior

Synthesis of original spherical α-Ni(OH) 2 architectures by microwave-assisted hydrothermal method and their in situ thermal convention to NiO

Hydrothermal Synthesis and Electrochemical Performance of NiO Microspheres with Different Nanoscale Building Blocks

Microwave Hydrothermal Synthesis Of Self-Assembled Nickel Hydroxide Microspheres

Preparation and characterization of nickel hydroxide microspheres assembled by nanoribbons

Solvothermal Preparation and Characterization of Nano-nickel Oxide

Microwave-Assisted Hydrothermal Synthesis of Ni(Oh)(2) Architectures and Their in Situ Thermal Convention to Nio

Surfactant-assisted Solvothermal Synthesis of Pure Nickel Submicron Spheres with Microwave-Absorbing Properties.

Fabrication of Novel Hierarchical Β-Ni(oh)2 and NiO Microspheres Via an Easy Hydrothermal Process

In Situ Hydrothermal Synthesis of Nickel Oxide Nanostructures by Thermal Decomposition and Its Electrochemical Property

Hydrothermal synthesis of α-Ni(OH) 2 and its conversion to NiO with electrochemical properties

Microwave Hydrothermal Synthesis and Characterizations of Nis Nano-Needle

Hydrothermal and Thermal Decomposition Synthesis of Hierarchical NiO Microspheres with Mesoporous Structure

Hydrothermal Synthesis of Β-Nickel Hydroxide Microspheres with Flakelike Nanostructures and Their Electrochemical Properties

Fabrication of Nickel Nitrate Hydroxide Microsphere with Inheriting Morphology to Β-Ni(oh)2 and NiO

Hydrothermal Synthesis and Performance Research of Nano - Sized Β-Ni (OH)2

Template-free Sonochemical Synthesis of Hierarchically Porous NiO Microsphere.

Single-crystal-like NiO colloidal nanocrystal-aggregated microspheres with mesoporous structure: Synthesis and enhanced electrochemistry, photocatalysis and water treatment properties

Submicrometer-sized NiO octahedra: Facile one-pot solid synthesis, formation mechanism, and chemical conversion into Ni octahedra with excellent microwave-absorbing properties

Microwave-assisted non-aqueous homogenous precipitation of nanoball-like mesoporous α-Ni(OH) 2 as a precursor for NiO x and its application as a pseudocapacitor