Effect and Mechanism of Natural Zeolite on Suppressing ASR in Concrete

Nai Qian Feng,Jia Huang,Tianyong Hao

DOI: https://doi.org/10.14359/6009

1998-01-01

Abstract:First Name is required invalid characters Last Name is required invalid characters Email Address is required Invalid Email Address Invalid Email Address

What problem does this paper attempt to address?

EFFECT AND MECHANISM OF NATURAL ZEOLITE ON SUPPRESSING ALKALI-SILICA REACTION (ASR) IN CONCRETE

Nai Qian Feng,Jia Hua,Tianyong Hao

1998-01-01

Abstract:Effect and mechanism of natural zeolite (NZ) on preventing expansion due to alkali-silica reaction (ASR) are studied in this paper. The reduction of deleterious expansion by NZ is compared with that of three other cementitious materials: silica fume (SF), fly ash (FA), and blast-furnace slag (BFS). The order of effectiveness is SF>NZ>FA>BFS. When 30% zeolite blended cement with an alkali content of 1.82% Na2O equivalent is used in concrete, there will be no damage from ASR even if all the aggregates are reactive. The suppression of ASR by NZ is related to its fineness. The required dosage of NZ is about 20% at a surface area of 7000 cm squared/g with the same effect. Pre-heating of NZ at 500 degrees C increases the preventive effectiveness. The suppressing mechanism of NZ on ASR is decreasing the alkali ion concentration in the pore solution in concrete through ion exchange, adsorption, and pozzolanic reaction of NZ. So the formation of alkali silicate is prevented and the interface is improved.
Effect of the Composite of Natural Zeolite and Fly Ash on Alkali-Silica Reaction

Feng Xiao-xin,Feng Nai-qian,Han Dong

DOI: https://doi.org/10.1007/bf02838402

2003-01-01

Journal of Wuhan University of Technology-Mater Sci Ed

Abstract:The effect of the composite of natural zeolite and fly ash on alkali-silica reaction (ASR) was studied with natural alkali-reactive aggregate and quartz glass aggregate respectively. The expansive experiment of mortar bar and concrete prism was completed. The results show that ASR can be suppressed effectively by the composite of natural zeolite and fly ash.
Effects of Natural Zeollite on the Restraining of Alkali-silica Reaction

FENG Nai-qian

DOI: https://doi.org/10.3969/j.issn.1000-4637.2006.06.001

2006-01-01

Abstract:The effect of natural zeolite on restraining alkali-silica reaction has been investigated through the tests of measuring the ion exchange capacity of natural zeolite with time,the hydration degree of natural zeolite and the influences of natural zeolite on alkali content in the pore solution.The results show that the ion exchange rate is of the highest at the first 10 minute,the ion exchange capacity reaches 80% of the total capacity in 2 hours and the exchange tends to equilibrium in about 2 days.In the case of cement being replaced by 30% of natural zeolite and the duration of hydration for 6 months,the hydration degree of natural zeolite is about 40%-50%.The ASR expansion is restrained by natural zeolite through reducing the water soluble alkali content and the effective alkali content.There is no disadvantage effect of the alkali in natural zeolite on restraining alkali-silica reaction,when the replacement level of cement by natural zeolite is more than a certain quantity.
Suppressing Effect of Superfine Mineral Powder on Alkali-Aggregate Reaction

牛全林,冯乃谦,谢威

DOI: https://doi.org/10.3969/j.issn.1007-0389.2004.05.004

2004-01-01

Abstract:The suppression effect of superfine mineral powder on ASR and ACR expansion was investigated according to ASTM C441 and the small concrete prism method respectively. It was shown that the addition of all the supplementary cementing materials such as slag, fly ash and zeolite were able to inhibit the ASR induced expansion, and the effect of metakaolin and zeolite were better than that of fly ash and slag's. The mineral powders were also beneficial for the control of ACR expansion, but not as effective as the suppression effect of ASR, the 28d expansion of the specimens incorporating 30% fly ash or 30% type A metakaolin were 0.0953% and 0.108% respectively, while the other specimens were ranging from 0.12% to 0.16%.
The Effect of Alkali-Silica Reaction (Asr) on the Mechanical Properties of Concretes Containing Trass

Ebrahim Ghiasvand,Afshin Mohammadi,Mahmoud Nili,Zahra Rezaei

DOI: https://doi.org/10.2139/ssrn.4184133

2022-01-01

SSRN Electronic Journal

Abstract:The Alkali-silica reaction (ASR) is one of the most significant concerns in the concrete life cycle. It reduces the serviceability and increases the expense of maintaining structures. In addition, the occurrence of ASR impacts the internal structure of concrete and decreases its integrity. Thus, the mechanical properties of concrete can be significantly affected by ASR. Different researchers have mentioned this issue, and most of the results have proved the reduction of the mechanical properties of concrete due to ASR. This paper studied the effect of ASR on concrete's three main mechanical properties (compressive, flexural, and tensile strength). In order to evaluate the aforementioned parameters, mixtures with and without Trass containing aggregates with varying degrees of reactivity were prepared and cured under various conditions. The results showed all studied properties decreased under ASR conditions (accelerated ASTM C1293 at 60 ºC). However, this reduction depended on the reactivity degree of the used aggregates. Furthermore, using the Trass as a partial replacement for cement could reduce ASR's destructive effects.
Use of natural zeolite as a supplementary cementitious material

Babak Ahmadi,Mohammad Shekarchi

DOI: https://doi.org/10.1016/j.cemconcomp.2009.10.006

IF: 9.93

2010-02-01

Cement and Concrete Composites

Abstract:Natural zeolite, a type of frame-structured hydrated aluminosilicate mineral, is used abundantly as a type of natural pozzolanic material in some regions of the world. In this work, the effectiveness of a locally quarried zeolite in enhancing mechanical and durability properties of concrete is evaluated and is also compared with other pozzolanic admixtures. The experimental tests included three parts: In the first part, the pozzolanic reactivity of natural zeolite and silica fume were examined by a thermogravimetric method. In this case, the results indicated that natural zeolite was not as reactive as silica fume but it showed a good pozzolanic reactivity. In the second part, zeolite and silica fume were substituted for cement in different proportions in concrete mixtures, and several physical and durability tests of concrete were performed. These experimental tests included slump, compressive strength, water absorption, oxygen permeability, chloride diffusion, and electrical resistivity of concrete. Based on these results, the performance of concretes containing different contents of zeolite improved and even were comparable to or better than that of concretes prepared with silica fume replacements in some cases. Finally, a comparative study on effect of zeolite and fly ash on limiting ASR expansion of mortar was performed according to ASTM C 1260 and ASTM C 1567. Expansion tests on mortar prisms showed that zeolite is as effective as fly ash to prevent deleterious expansion due to ASR.

construction & building technology,materials science, composites
Solidification of low-level-radioactive resins in ASC-zeolite blends

Li Junfeng,Zhao Gang,Wang Jianlong

DOI: https://doi.org/10.1016/j.nucengdes.2004.10.008

IF: 1.7

2005-01-01

Nuclear Engineering and Design

Abstract:Solidification of low-level-radioactive (LLR) resins was studied in ASC (a kind of new cement)-zeolite blends. The effect of addition of zeolite on the strength of the cementation matrix was investigated. A superior combination was obtained as ASC 35wt.%, zeolite 7wt.% to mix 42wt.% of resins with 16wt.% of water, the moisture content of the resins was about 50%. The simulated leaching tests showed that inclusion of zeolite in ASC reduced the leaching rates of radionuclides significantly. From tests of 200L, the center temperature curve was measured, and no early thermal cracks were found.
Modelling of Effect of ASR on Concrete Microstructure

O. Çopuroğlu,E. Schlangen

DOI: https://doi.org/10.4028/www.scientific.net/KEM.348-349.809

2007-07-29

Abstract:In the present study the damage mechanism of Alkali-Silica-Reaction (ASR) in concrete bearing reactive volcanic rock is investigated. A combined numerical and experimental research is presented. The mechanism of ASR is investigated on a concrete microbar specimen by using various microscopy techniques. A meso mechanical model based on lattice theories is used as a starting point. Variables in the model are the properties of the concrete components on the meso-level, like mechanical properties of cement paste, aggregates, dissolved aggregate, bond properties and finally the properties of the gel. It is found that current numerical model is able to simulate ASR cracks similar to the experimental observations.

Engineering,Materials Science
Failure criteria and microstructure evolution mechanism of the alkali–silica reaction of concrete

Yongbo Wang,Peng Gao,Huaizhi Su,Yuanyu Qin,Yimeng Wang,Gang Xue

DOI: https://doi.org/10.1515/rams-2023-0102

2023-01-01

REVIEWS ON ADVANCED MATERIALS SCIENCE

Abstract:Abstract In this study, the influence of two distinct reactive aggregate dosages on the alkali–silica reaction (ASR) of concrete was investigated. The expansion ratio, axial compressive strength, splitting tensile strength, and relative dynamic elastic modulus (RDEM) of concrete were considered as the main parameters to study the failure criteria of concrete induced by ASR at 40°C. Microscopic experiments, such as scanning electron microscopy and X-ray computed microtomography, were applied to analyze the damage induced by ASR on the concrete prisms and the propagation of internal cracks of the reactive aggregates in nanospace. The results showed that the two ranges can be used as the failure criteria produced by the ASR of concrete containing 3 and 6% dosages of reactive aggregates at 40°C, respectively, when the RDEM of concrete was reduced to 70‒75% and 85‒90%. Additionally, the results of CT indicated that microcracks tended to extend from the initial defects of aggregate to the cement slurry. Meanwhile, ASR gel packed with the pores, which reduced the porosity. It was noteworthy that the adhesive force between the ASR gel and the cement matrix after filling pores could not make up for the loss of the mechanical properties of concrete.

materials science, multidisciplinary,nanoscience & nanotechnology
Effect of ASR expansion on mechanical properties of concrete

Alkan Hafci,Lutfullah Turanli,Fatih Bektas

DOI: https://doi.org/10.32047/cwb.2021.26.1.2

2021-01-01

Cement wapno beton

Abstract:In this experimental study the effect of alkali silica reaction [ASR] on the mechanical properties of concrete namely compressive strength, fl exural strength, splitting tensile strength, modulus of elasticity and pull-out strength is presented. The effect of the specimens’ geometry on ASR expansion has also been studied. The results confirm that ASR expansion of over 0.04% causes significant losses in the mechanical properties of concrete, albeit at differing rates. Moreover, this study proves that the specimen geometry has an important role on ASR expansion rate.

construction & building technology,materials science, composites
Research Progress in Effect of Lithium Salts Inhibiting Alkali-Silica Reaction

Z. Shiping

Abstract:ASR is one of the most important factors effecting the concrete durability and it becomes the global disaster problem in recent years.Many researchers have done a great deal of works about how to preventing and inhibiting the alkali-aggregate reaction.In this paper the research work on the mechanism and the suppressive effects of lithium salts inhibiting the expansion due to the alkali-silica reaction(ASR) in concrete and the research progress in this field during the past years are reviewed.In addition,the further work needed for practical application is discussed.

Engineering,Materials Science
Numerical and experimental study of ASR in concrete at the meso-level

J. Liaudat,C. Garello,I. Carol

DOI: https://doi.org/10.21012/FC9.287

2016-05-29

Abstract:In this paper, an ongoing research project on the mechanisms of concrete deterioration due to Alkali-Silica Reaction (ASR) is presented, together with some preliminary results. The research program includes both experimental and numerical modelling work. The first part includes the development of two new experimental setups, one devoted to study the ASR expansion mechanisms at the level of a single matrix-aggregate interface and the other to the study of ASR expansions of cubic concrete specimens under triaxial confinement. The second part includes the formulation and numerical implementation of a chemo-mechanical model for ASR expansions in concrete at the meso-level. The model considers three main diffusion/reaction field equations for the concentrations of silicates, calcium and alkalis in concrete pore solution, complemented by a number of chemical kinetics and chemical equilibrium equations. The volume fraction distribution of the solid constituents of the hardened cement paste and the reaction products evolve with the progress of the reaction, determining the diffusivity properties of the material and, eventually, inducing expansions.

Engineering,Materials Science
Effect of nano-silica as cementitious materials-reducing admixtures on the workability, mechanical properties and durability of concrete

Changjiang Liu,Xin Su,Yuyou Wu,Zhoulian Zheng,Bo Yang,Yuanbing Luo,Jingwei Yang,Jiangying Yang

DOI: https://doi.org/10.1515/ntrev-2021-0097

2021-01-01

Nanotechnology Reviews

Abstract:Abstract Nano-silica (NS) is one of the most important nanomaterials in recent years. It is used as a new cement-based composite reinforcement in building materials because of its high volcanic ash activity. In order to achieve the goal of carbon peaking and carbon neutralization, combined with the research idea of cementitious materials-reducing admixture for concrete, under the condition of reducing the amount of cement in concrete by 20%, the influence of different dosages of NS on the setting time and mechanical properties of concrete was analyzed. In addition, the shrinkage performance, impermeability, and resistance to chloride-ion permeability of concrete were also studied. The results show that under the same curing conditions and ages, when the NS dosage is 2.5%, the compressive strength and splitting tensile strength of the specimen after 28 days of curing are the highest, reaching 40.87 and 3.8 MPa, which show an increase by 6.6 and 15.15%. The shrinkage performance of concrete increases with the increase in NS dosage. In addition, when the NS dosage is 2.0%, the durability of concrete has also been greatly improved. The impermeability of concrete increased by 18.7% and the resistance to chloride-ion permeability increased by 14.7%. Through microscopic analysis it was found that NS can promote the hydration reaction, generate more hydration products such as calcium silicate hydrate (C–S–H), enhance the interfacial adhesion between the matrix and the aggregate, and form a closer interfacial transition zone. Moreover, the addition of NS also reduces the cumulative pore volume in concrete, refines the pore size, and makes the internal structure of concrete denser.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry
Nano-scale structure and mechanical properties of ASR products under saturated and dry conditions

Huite Wu,Jianwen Pan,Jinting Wang

DOI: https://doi.org/10.1038/s41598-020-66262-9

IF: 4.6

2020-06-08

Scientific Reports

Abstract:Abstract Alkali-silica reaction (ASR) widely occurs in concrete, resulting in durability problem and premature loss in serviceability of infrastructures all over the world. Understanding of the properties of ASR products, especially at micro scale level, helps mitigation of deterioration in concrete structures. In this study, the nano-scale structure and mechanical properties of the ASR products under dry and saturated conditions are investigated. The scanning electron microscope and energy dispersive spectrometer with X-ray (SEM-EDS) and atomic force microscope (AFM), as well as the nanoindentation are applied to the ASR products. The experimental observation indicates the effect of water on the micromorphology and nano-scale mechanical properties of ASR products. Water makes contribution to the transformation of ASR products from solid to viscous gels and the decrease in the Young’s modulus and hardness of ASR products. The testing results reveal the correlation between nano-scale structure and mechanical properties and improve the understanding of the micromechanical behavior of ASR products.

multidisciplinary sciences
Mechanical Properties of Aeolian Sand Concrete Made from Alkali-Treated Aeolian Sand and Zeolite Powder

Lisi Wei,Zhanquan Yao,Hao Li,Haolong Guo,Yue Li

DOI: https://doi.org/10.3390/ma17071537

2024-03-28

Abstract:The aim of this study is to promote the application of the excited zeolite powder (ZP)with aeolian sand powder (ASP) in the field of aeolian-sand concrete (ASC) production. This study utilises NaOH to treat composite cementitious materials containing aeolian sand and zeolite powders, which were used to replace 50% of the cement in aeolian-sand concrete (ASC). Production of alkali-inspired cement-based windswept concrete(AAZC).The mechanical properties of treated ASC considerably improved, especially when the NaOH dosage was 4% by mass. After curing this sample (denoted as AAZC-4) for 28 d, its compressive strength improved by 17.2%, and its split tensile increased by 16.3%. Potassium feldspar and montmorillonite in zeolite powder and SiO2 in the sand were decomposed by OH- and combined with other elements to generate various silicate gels and A-type potassium zeolite crystals inside the concrete. Microscopic examination showed that the gels and crystals intertwined to fill the pores, decreasing (increasing) the percentage of large (small) pores, thus optimising the pore structure. This substantially improved the mechanical properties of ASC. Freeze-thaw salt-intrusion tests showed that the extent of mass loss, degree of damage and loss of compressive strength of AAZC-4 were similar to those of ordinary concrete but were reduced by 36.8%, 19% and 52.1%, respectively, compared with those of ASC. Therefore, AAZC-4 has a sustainable working performance in chloride-ion permeable environments in cold and arid areas.
Frost Resistance of Internal Curing Concrete with Calcined Natural Zeolite Particles

Xuan Zheng,Jun Zhang,Xiaoping Ding,Hewei Chu,Jiajia Zhang

DOI: https://doi.org/10.1016/j.conbuildmat.2021.123062

IF: 7.4

2021-01-01

Construction and Building Materials

Abstract:In this paper, the frost resistance of internal curing concrete with calcined zeolite particles was studied, comparing with ordinary curing concretes. Concrete specimens with compressive strength of 50 MPa and 100 MPa were prepared. Firstly, the pore structure characteristics of the concrete specimens were tested by mercury intrusion porosimetry. Then freeze-thaw test was conducted, residual deformation, weight loss and strength loss of concrete specimens during freeze-thaw cycles were measured to investigate the frost resistance of the specimens, and water saturation degree of the specimens during freeze-thaw cycles was tested to analyze the mechanism of frost resistance. Results show that, the porosity and pore structure of concrete can be improved by prewetted zeolite particles with the development of curing age. For the same water absorption time, the water saturation of zeolite curing concrete is higher than that of ordinary curing concrete in the initial stage of freeze-thaw cycles, but the growth rate with the develop-ment of freeze thaw cycles is much slower. The frost resistance of concrete using calcined zeolite is slightly worse than that of ordinary curing concrete in early stage of freeze-thaw cycles, while it is much better in the middle and later stage. (c) 2021 Elsevier Ltd. All rights reserved.
Mechanical Properties of ASR-Affected Concrete Containing Fine or Coarse Reactive Aggregates

B. Fournier,S. Dean,B. Durand,B. Bissonnette,M. Bérubé,N. Smaoui

DOI: https://doi.org/10.1520/JAI12010

Abstract:This experimental study was conducted to investigate the effects of the alkali-silica reactivity (ASR) on the mechanical properties of concrete, and in particular the strength and the modulus of elasticity under direct tension. Two highly reactive aggregates, a coarse (Quebec City limestone) and a fine (Texas sand) were used. The results suggest that the effects of ASR on the mechanical properties of concrete may vary with the reactive aggregate involved. At least, they depend on the particle size and/or the degree of reactivity of this aggregate. The direct tensile strength was the mechanical property of concrete, the most affected and the most-rapidly affected by ASR. At 0.1 % expansion, for instance, concrete cylinders cast with the Quebec City limestone showed moderate losses of 16 % in compressive strength and in splitting strength (Brazilian test), but as high as 48 % in direct tensile strength. The modulus of elasticity presented similar values in compression and in direct tension, and its reduction also gives a very good idea of the progress of the damage due to ASR. At 0.1 % expansion, for instance, concrete cylinders containing the Quebec City limestone showed a loss in modulus of 19 % in direct tension and 23 % in compression.

Engineering,Materials Science
Study on the Effect and Mechanism of Alkali–Silica Reaction Expansion in Glass Concrete

Da Huang,Pengliang Sun,Pengfei Gao,Guangyan Liu,Yuanhao Wang,Xuandong Chen

DOI: https://doi.org/10.3390/su131910618

IF: 3.9

2021-09-24

Sustainability

Abstract:The suppression of ASR expansion hazards of glass concrete has always been a key and hot issue in the research of glass concrete. According to the ASTM C1260-14 fast mortar rod method, glass sand and glass powder act as fine aggregate and auxiliary cementing material, respectively. The changes in expansion rate with different amounts of glass sand content and different particle sizes of glass powder in mortar rods were compared, and the effects of glass sand content and the glass powder particle size on the expansion of ASR were analyzed. SEM was used to compare and analyze the microstructure of mortar rods to explore the mechanism of ASR expansion of glass concrete, and the results showed that the addition of glass powder had a certain inhibitory effect on ASR expansion. The larger the particle size of glass powder was, the better the inhibition effect on ASR expansion and the longer its duration. Compared with the three groups of experiments of 0–13 μm, 13–38 μm, and 38–75 μm, it was found that the influence of the glass powder particle size on the expansion of ASR was weaker than that of dosage. The inhibitory effect of glass powder on ASR expansion is related to the fact that glass powder is more involved in pozzolanic reaction in the early hydration process.

environmental sciences,environmental studies,green & sustainable science & technology
Mechanical properties of ASR affected concrete: a critical review

V. Sirivivatnanon,Nadarajah Gowripalan,Jianchun Li,Yan-gui Yu,T. N. Nguyen

2019-09-08

Abstract:Alkali-silica reaction (ASR) in concrete can induce degradation to its mechanical properties, leading to compromised serviceability and even loss in load carrying capacity of concrete structures. Considering the importance of the problem, extensive studies mostly by means of experimental investigations have been carried out to gain understanding on impacts of ASR on the mechanical properties on both plain and reinforced concrete specimens. This paper presents a state-of-the-art literature review on published research related to mechanical properties of ASR-affected concrete, including mechanisms, influencing factors and evaluation procedures. In order to gain an insight into the effects of ASR on mechanical properties, a database has been established from a large number of experimental data published in open literature. Various empirical models that are commonly used to estimate the mechanical properties through measured ASR expansions are also reviewed and examined for their accuracy using the established database.

Engineering,Materials Science
Experiment study on the mechanical properties and alkali silica reaction (ASR) of mortar blended rice husk ash (RHA)

Zhiyao Ma,Hairong Huang,Xinying Hu,Haiping Yang

DOI: https://doi.org/10.1016/j.cscm.2023.e02028

IF: 4.934

2023-03-31

Case Studies in Construction Materials

Abstract:To ensure the serviceable popularization of RHA and avoid the alkali silica reaction of mortar blended RHA, the impact of RHA particle size and dosage on the mechanical strength and alkali silica reaction expansion of the mortar prepared with nonreactive silica sand and river sand has been evolutionarily investigated. The hydrates products of the mortar containing RHA were conducted by thermogravimetric (TG) and X-ray diffraction analysis (XRD). The microstructure of the mortar containing RHA was also explored by scanning electron microscope with an energy-dispersive X-ray spectroscopy analysis (SEM-EDX). The experiment results demonstrate that the compressive strength of mortar could be maximum enhanced by 21.1 % when RHA8.8 substituted 20 % of cement due to the pozzolanic effect and physical filling effect of RHA. Moreover, RHA with massive amorphous silica could react with Na ions in pore solution to form alkali-silica gel, thereafter resulting in expanding and destroying the microstructure of the mortar. The real ASR expansion value fabricated by RHA increased as the RHA particle size increased, which was mostly up to 0.0177 % when 20 % cement was replaced by RHA with a mean particle of 27.6 μm. Cracks noticeably emerged on the surface and edge of the mortar containing RHA with the particle size from 8.8 μm to 27.6 μm when RHA substituted 20 % of cement (by mass). Overall, the RHA particle size should be lower than 8.8 μm, while the substitution of cement by RHA also be below 10 % of cement, which can safely avoid the destructive expansion of RHA in an alkali environment.

construction & building technology,materials science, multidisciplinary,engineering, civil

Effect and Mechanism of Natural Zeolite on Suppressing ASR in Concrete

EFFECT AND MECHANISM OF NATURAL ZEOLITE ON SUPPRESSING ALKALI-SILICA REACTION (ASR) IN CONCRETE

Effect of the Composite of Natural Zeolite and Fly Ash on Alkali-Silica Reaction

Effects of Natural Zeollite on the Restraining of Alkali-silica Reaction

Suppressing Effect of Superfine Mineral Powder on Alkali-Aggregate Reaction

The Effect of Alkali-Silica Reaction (Asr) on the Mechanical Properties of Concretes Containing Trass

Use of natural zeolite as a supplementary cementitious material

Solidification of low-level-radioactive resins in ASC-zeolite blends

Modelling of Effect of ASR on Concrete Microstructure

Failure criteria and microstructure evolution mechanism of the alkali–silica reaction of concrete

Effect of ASR expansion on mechanical properties of concrete

Research Progress in Effect of Lithium Salts Inhibiting Alkali-Silica Reaction

Numerical and experimental study of ASR in concrete at the meso-level

Effect of nano-silica as cementitious materials-reducing admixtures on the workability, mechanical properties and durability of concrete

Nano-scale structure and mechanical properties of ASR products under saturated and dry conditions

Mechanical Properties of Aeolian Sand Concrete Made from Alkali-Treated Aeolian Sand and Zeolite Powder

Frost Resistance of Internal Curing Concrete with Calcined Natural Zeolite Particles

Mechanical Properties of ASR-Affected Concrete Containing Fine or Coarse Reactive Aggregates

Study on the Effect and Mechanism of Alkali–Silica Reaction Expansion in Glass Concrete

Mechanical properties of ASR affected concrete: a critical review

Experiment study on the mechanical properties and alkali silica reaction (ASR) of mortar blended rice husk ash (RHA)