Chain Conformation and Liquid-Crystalline Structures of a Poly(thieno)thiophene
Chang Liu,Wenhong Yang,Hanqiu Jiang,Baoqing Zhang,Guoming Liu,Erqiang Chen,Dujin Wang,François Boué
DOI: https://doi.org/10.1021/acs.macromol.2c00143
IF: 5.5
2022-03-11
Macromolecules
Abstract:The chain conformation and solid-state structure of conjugated polymers are important for understanding the structure origin of electronic properties. In this work, a high-performance conjugated polymer, poly(2,5-bis(2-thienyl)-3,6-ditetradecylthieno[3,2-b]thiophene) (PBTTT_C14), is chosen. The chain conformation of PBTTT_C14 in a good solvent (1,2-dichlorobenzene) in the dilute condition is characterized by small-angle neutron scattering (SANS). The persistence length of PBTTT_C14 is estimated as 4.3 ± 0.3 nm, indicating a more rigid backbone compared with poly(3-hexylthiophene-2,5-diyl) (P3HT). In addition, the structural evolution of PBTTT_C14 in bulk was studied in detail. Three transitions are detected during heating, located at 57 °C (Tm1), 133 °C (peak A), and 223 °C (Tm2). Fourier transform infrared spectroscopy (FTIR) results show that a transition from the trans- to gauche-conformation of the side chains occurs at Tm1, corresponding to the melting of the regular packing of the side chains. After that, the system enters liquid crystal states. Oriented films are obtained by shear within the liquid-crystalline phases, in which the backbones align along the shear direction. After assignment of the FTIR bands, it is found that the twist motion of thienothiophene rings in the backbone is activated at peak A. Two liquid-crystalline (LC) phases with different structures at the temperature range of Tm1 ∼ peak A (LC-1) and peak A ∼ Tm2 (LC-2) are determined for PBTTT_C14: the twist motion of backbones leads to an enhanced lamellar order, weaker interchain π–π interaction and vanishes the positional order along the chain axis (disappearance of (003)) for LC-2.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.macromol.2c00143.Experimental details of the rheological measurement, SANS analysis using Zimm plots, Rg correction for excluded volume effect, DFT calculation, additional FTIR and WAXS results, and analysis of the rheological results (PDF)This article has not yet been cited by other publications.
polymer science