Abstract:The wetting and spreading behaviors of pure nickel and nickel based alloys on sintered ZrB2-SiC ceramics and their interfacial microstructures were investigated in this presentation. The nickel-based alloys were mainly the commercial nickel-molybdenum-chromium products. The wetting and spreading properties were observed by a real-time thermal optical measurement system under flowing argon-5%hydrogen atmosphere. As temperature increased, the pure nickel cylinder sample on ZrB2-SiC substrate had few changes before 1228°C except for the thermal expansion in size. After that, liquid phase formed and spread gradually on the ceramic substrate. The contact angle was about 15o after holding 15min at 1600°C. Therefore, pure nickel could contact sintered ZrB2-SiC ceramics well. Meanwhile, the introduction of molybdenum and/or chromium in the pure nickel was beneficial for the wetting of nickel on sintered ZrB2-SiC ceramics. The contact angles of Ni-28Mo and Ni-16Mo-23Cr alloys on sintered ZrB2-SiC ceramics after 1600°C/15min were 13o and 2o, respectively. In addition, the temperatures of the liquid drop formed rose obviously in contrast to the pure nickel. The SEM images indicated that the interfacial microstructures of Ni-based alloys on sintered ZrB2-SiC ceramic substrates were uniform and the dissolved boundaries showed that they had a good bonding. However, some cracks were found in the Ni/ZrB2-SiC system for their high thermal mismatch. On the other hand, the Ni-Mo (-Cr)/ZrB2-SiC interface had few defections and evident elemental diffusion between the ceramic substrates and the alloys were found at the interface.

Insight into the Wetting Behavior and Interfacial Evolution of Sn-xZr/ZrO2 Systems at 850-950 ℃

Wetting and Interfacial Behavior of Sn–Ti Alloys on Zirconia

Reactive Wetting and Interfacial Characterization of ZrO2 by SnAgCu-Ti Alloy

Influence of water content in mixed solvent on surface morphology, wettability, and photoconductivity of ZnO thin films.

Temperature Dependence of the Wettability Between Glass‐Forming Alloy Zr55Cu30Al10Ni5 and Polycrystalline ZrO2

Reactive wetting and infiltration of polycrystalline WC by molten Zr2Cu alloy

Wetting and Interfacial Phenomena Between a Ni-based Superalloy and Silica-Based Ceramic Cores with ZrSiO4 Additions

Wetting Behaviors of Pure Nickel and Nickel-Based Alloys on Sintered ZrB2-SiC Ceramics

Sn behavior over Si_3N_4/2024Al composite surface in wetting test of Sn-Zn alloy

Wetting Behavior and Interfacial Characteristics in the Molten Bi-Sn/High-Entropy Alloy System

Wettability and spreading behavior of Sn–Cr alloys on SiC

Influence of solution concentrations on surface morphology and wettability of ZnO thin films

Wetting and Low Temperature Bonding of Zirconia Metallized with Sn0.3Ag0.7Cu-Ti Alloys

Wetting of silica and 304 stainless steel by SnO-P2O5-ZnO glass at 500–600 °C

Reactive wetting and interfacial reaction mechanism of ZrC-SiC ceramic and Ag-Zr filler

Revealing the Mechanism of Abruptly Dropping of the Wetting Angle for the Cast Iron and Zirconia Ceramic System

Reaction Induced Anomalous Temperature Dependence of Equilibrium Contact Angle of TiZr Based Glass Forming Melt on Al2O3 Substrate

Spontaneous infiltration and wetting behaviors of a Zr-based alloy melt on a porous SiC substrate

Wettability of molten titanium in Ti/zirconia system

Reactive Wetting of Tic-Ni Cermet by Ag-Cu-Zn Alloy During Evaporation

Wetting and Spreading Behavior of Sn–Ti Alloys on SiC