Thermally Stable Phenylethylammonium-based Perovskite Passivation: Spontaneous Passivation with Phenylethylammonium Bis(trifluoromethylsulfonyl)imide under Deposition of PTAA for Enhancing Photovoltaic Performances of Perovskite Solar Cells

Naoyuki Nishimura,Hiroyuki Kanda,Ryuzi Katoh,Takurou N. Murakami

DOI: https://doi.org/10.26434/chemrxiv-2023-0wrzg

2023-12-29

Abstract:Perovskite passivation has been vital for obtaining highly efficient and stable perovskite solar cells (PSCs). Phenylethylammnonium (PEA)-based passivator is one of the most major categories as it is effective in improving PSC performances taking advantages of its large absorption energy over perovskite surface. However, this conventional passivator suffers from thermal stability issues; under thermal stress even at moderate temperature (e.g., 50℃) for several minutes, the overlayer of the perovskite passivated with PEA iodide salt (PEAI) transforms to a two-dimensional perovskite of (PEA)2PbI4, which hampers carrier transfer, thus negating the passivation effects and/or degrading the photovoltaic (PV) performances. Herein, we propose a novel yet simple strategy to address the thermal stability issue using a newly synthesized PEA bis(trifluoromethylsulfonyl)imide (PEA-TFSI) additive for poly[bis(4-phenyl)(2,4,6-trimethylphenyl)amine (PTAA) hole transport materials (HTMs). Upon the deposition of the PTAA HTM solution with a PEA-TFSI additive over the perovskite layers, the PEA cations spontaneously passivated the perovskite, forming a monolayer-like passivation overlayer. The resulting PEA-based passivation did not cause crystallization at the elevated temperature of 85℃; hence, it did not cause PV performance drop due to the thermal stress and retained a higher PV performance compared to the samples with the conventional Li-TFSI additive for over 800 h. Besides, compared to PSCs with Li-TFSI, PSCs with PEA-TFSI exhibited an improvement in stability under humid conditions (30℃, 50% relative humidity) for over 600 h, taking advantage of the resulting hydrophobicity. The optimal PEA-TFSI additive enhanced the PV performance, reaching a power conversion efficiency of up to 22.1% (21.2% in the quasi-steady state). These values are relatively high in the PTAA-based PSCs with an n-i-p structure particularly without using lithium species, which is considered to be detrimental for PSCs. These high PV performances were most likely attributed to improved affinity at the interface between PTAA and the perovskite, which is hardly attainable by an aliphatic ammonium passivator, and the PEA passivation effects. These results provide novel insights into the commonly used PEA-based perovskite passivation particularly in combining thermally stable PTAA HTMs and the promising alkylammonium spontaneous passivators, which spurs the further development of PSCs.

Chemistry

What problem does this paper attempt to address?

This paper mainly discusses how to solve the thermal stability issue of the phenylethylammonium (PEA)-based passivation layer in perovskite solar cells (PSCs). Traditionally, PEA iodide salt (PEAI) is used as a passivating agent to improve the performance of the cells, but it transforms into two-dimensional perovskite under heating, affecting charge carrier transport and reducing photovoltaic performance.

The researchers propose a novel strategy, which is to use newly synthesized PEA bis(trifluoromethanesulfonyl)imide (PEA-TFSI) additive in combination with poly[bis(4-phenyl)(2,4,6-trimethylphenyl)amine] (PTAA) hole transport material (HTM). When depositing the PTAA HTM solution, PEA cations spontaneously passivate the perovskite, forming a monolayer passivation top layer. This method avoids crystallization at 85°C, so there is no performance degradation under thermal stress, and it displays over 800 hours of high photovoltaic performance on samples containing Li-TFSI. In addition, the PEA-TFSI additive also improves stability under humidity conditions by resisting humidity effects due to its hydrophobicity.

Experimental results show that the PEA-TFSI additive enhances photovoltaic performance, achieving a power conversion efficiency of up to 22.1% (21.2% under steady state) which is quite high for PTAA-based n-i-p structure PSCs without lithium species. The study also reveals that PEA-TFSI passivation improves the interface affinity between PTAA and perovskite, which is achieved by the PEA passivating agent and cannot be achieved by traditional alkylamine passivating agents.

In conclusion, this paper aims to address the thermal stability issue of PEA-based passivating agents and proposes a simple method to achieve stable and efficient PTAA HTM passivation using PEA-TFSI additives, providing new insights and avenues for further development of PSCs.