A Novel ZIF-8 and ZIF-67 Co-Modified TiO2 Nanospheres for Highly Efficient Degradation of Methylene Blue under Simulated Sunlight

Hanyong Cai,Juan Gao,Jiale Deng,Lingcheng Zheng,Mei Liu,Pingping Wei,Yanfen Wang,Yang Li

DOI: https://doi.org/10.1007/s10854-023-11697-9

2023-01-01

Journal of Materials Science Materials in Electronics

Abstract:In this work, a novel ZIF-8 and ZIF-67 co-modified TiO2 nanospheres with highly efficient degradation of organic pollutants was synthesized successfully. The structure, morphology, and chemical components of ZIF-8-67@TiO2 were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffractometer, infrared spectroscopy, and X-ray Photoelectron Spectroscopy. The optical properties of all samples were analyzed by UV–Visible diffuse reflectance spectroscopy diffraction. It is found that after the growth of ZIFs on the surface of TiO2 nanospheres, the specific surface area of TiO2 was greatly improved. The light sensitivity area of TiO2 is extended to include both the visible and ultraviolet spectrums by loading ZIF-8 and ZIF-67 nanoparticles. In addition, the construction of Z-scheme heterojunction also improves the separation of photocarriers, and the transfer of photogenerated charges between ZIFs and TiO2 is accelerated by the formed N–Ti–O bonds, thus extending the lifetime of photogenerated charges and enhancing the catalytic activity. The ternary ZIF-8-67@TiO2 demonstrates excellent photocatalytic activity and photoelectrochemical performance. The corresponding first-order kinetic constant (16.56 × 10−3 min-1) of ZIF-8-67@TiO2 is 11.6 times more than that of TiO2(1.43 × 10−3 min−1). Especially, in strong alkaline environment (pH = 12), methylene blue can be almost completely degraded within 15 min. Furthermore, ZIF-8-67@TiO2 exhibits the maximum photocurrent density (36.69 µA/cm2), which is 15.7 times greater than that of TiO2 (2.33 µA/cm2). Therefore, the co-modified TiO2 nanospheres with ZIF-8 and ZIF-67 can serve as a promising route to fabricate photocatalytic membranes for use in the water treatment industry.