Abstract:Achieving ultra-high tensile yield strength over 400 MPa in RE modified Mg-Zn-based alloys using conventional thermomechanical processing is a challenging task. In this study, we successfully produced a Mg-7Zn-2Gd-0.5Zr (wt. %) alloy with exceptional strength through traditional hot-extrusion techniques. This alloy exhibits a tensile yield strength of 440 MPa and an acceptable ductility of 4.5%, surpassing a majority of previously reported Mg-Zn-RE-based alloys. Our findings demonstrate that the addition of Gd in Mg-Zn-based alloys effectively retards dynamic recrystallization (DRX) during extrusion, leading to the formation of a distinctive bimodal structure comprising approximately 13.8% coarse un-recrystallized (unDRXed) grains and about 86.2% fine DRXed grains. Furthermore, the alloying effect of Gd enhances particle density, including micron-sized particles and dynamic nano-precipitates. These dynamic precipitates play a crucial role in impeding dislocation movement during extrusion, thereby contributing to the formation of bimodal structure. Additionally, both nanoprecipitates and segregation of Zn and Gd atoms towards grain boundaries facilitate the formation of fine DRXed grains through pinning effect. Consequently, the significantly increased tensile yield strength observed in our Gd-modified alloy can be attributed to multiple strengthening mechanisms: fine DRXed grains, strong texture exhibited by unDRXed grains, numerous dynamic precipitates, high-density residual dislocations, and cosegregation of solutes. However, the formation of bimodal structure worsens the yield asymmetry of the Gdmodified alloy due to its strong basal texture. These results provide a valuable insight for further development efforts aimed at achieving ultra-high-strength Mg-Zn-RE-based alloys.

Ultra-high Tensile Strength Induced by Multiple Precipitates in Extruded ZK60 Alloy Via Co-Alloying Ca and Er

Effects of minor Nd and Er additions on the precipitation evolution and dynamic recrystallization behavior of Mg–6.0Zn–0.5Mn alloy

Realizing ultra-fine grains and ultra-high strength in conventionally extruded Mg-Ca-Al-Zn-Mn alloys: The multiple roles of nano-precipitations

Evolution of Bimodal-Structure and Achieving Ultra-High Yield Strength in the As-Extruded ZK70 Alloy Via Gd Addition

Achieving high strength above 400 MPa in conventionally extruded Mg-Ca-Zn ternary alloys

Microstructure and mechanical properties of extruded ZK60 magnesium alloy containing rare earth

Achieving a high-strength ZK60 alloy by introducing nano solute clusters

Influence of Secondary Extrusion on Microstructures and Mechanical Properties of ZK60 Mg Alloy Processed by Extrusion and ECAP

Tensile Properties of Extruded ZK60–RE Alloys

Dynamic precipitation and enhanced mechanical properties of ZK60 magnesium alloy achieved by low temperature extrusion

Achieving Ultra-High Strength in Mg–Gd–Ag–Zr Wrought Alloy Via Bimodal-Grained Structure and Enhanced Precipitation

Ultra-high strength Al-Zn-Mg-Cu alloys with high zinc content prepared via powder hot extrusion

Ultrastrong and Ductile Al-Mg Alloy Matrix Composites Via Composition-Modulated Precipitation Induced by Intragranular Ceramic Nanoparticles

Microstructure, Tensile Properties and Work Hardening Behavior of an Extruded Mg–Zn–Ca–Mn Magnesium Alloy

Ultrahigh Strength Mg-Al-Ca-Mn Extrusion Alloys with Various Aluminum Contents

Achieving High Strength-Ductility Synergy in Low-Alloyed Mg-Li-Er Extrusion Alloys via Tailoring Bimodal-Grained Structure

Ultra strength-ductility synergy in the Mg-Al-Zn alloy via densely dispersed multi-scale {1012‾} tension twins

Ultra strength-ductility synergy in the Mg-Al-Zn alloy via densely dispersed multi-scale {10<mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" altimg="si1.svg"><mml:mrow><mml:mover accent="true"><mml:mn>12</mml:mn><mml:mo>¯</mml:mo></mml:mover></mml:mrow></mml:math>} tension twins

Development of High-Strength, Low-Cost Wrought Mg–2.5mass% Zn Alloy Through Micro-Alloying with Ca and La

Ultrahigh Strength As-Extruded Mg–10.3Zn–6.4Y–0.4Zr–0.5Ca Alloy Containing W Phase

Enhanced Strength‐Ductility Synergy of Mg‐6Zn Alloy Wire by Inducing GP Zone Precipitation