Effect of Ca2+ doping on the upconversion luminescence properties of NaYF4:Yb3+/Tm3+ nanoparticles and its application to fluorescence temperature characteristics
Mingzhou Meng,Rui Zhang,Zhenlong Cheng,Xinmeng Fa,Jianghua Yang,Anees A. Ansari,Jun Ou,Christian Wurth,Ute Resch-Genger,mingzhou Meng,Rui zhang,Anees Ahmad Ansari,Christian Würth
DOI: https://doi.org/10.1039/d2ce00562j
IF: 3.756
2022-05-27
CrystEngComm
Abstract:The solvothermal method prepared a series of Yb3+/Tm3+/Ca2+ co-doped NaYF4 nanoparticles with different Ca2+ contents. Strong upconversion blue fluorescence could be observed under 980 nm laser excitation of the samples. The effect of different Ca2+ contents on the luminescence intensity was investigated, and it was found that the UV-to-visible upconversion luminescence increased and then decreased with increasing Ca2+ concentration during the increase of Ca2+ content from 0 mol% to 25 mol%, reaching the strongest fluorescence at 15 mol%, which was up to about 28 times stronger than that without Ca2+ doping. Furthermore, the mechanism was investigated, and it was found that the doping of Ca2+ disrupted the symmetry of the crystal field, resulting in a significant enhancement of the overall fluorescence. Applied to fluorescence intensity ratio thermometry, the absolute and relative sensitivities are as high as 0.0418 K-1 and 2.31% K-1, respectively, with a minimum temperature resolution of 0.0129 K.
chemistry, multidisciplinary,crystallography