Microstructural Characteristics Evolution of Asphalt Mastics under Cyclic Environmental Temperature Variations

Huining Xu,He Zhan,Meng Wang,Yiqiu Tan

DOI: https://doi.org/10.1016/j.conbuildmat.2023.132795

IF: 7.4

2023-01-01

Construction and Building Materials

Abstract:Environmental temperature-effect is the primary factor responsible for asphalt pavement failure. Asphalt pavement exposed to the atmosphere is constantly subjected to the thermal cycles induced by environmental temperature fluctuations, and the resulting thermal cracks significantly reduce the durability of asphalt pavement. Nevertheless, the influence of cyclic temperature variations on the performance degradation of asphalt binder materials is often overlooked. To address this, accelerated thermal cycling test was conducted on two asphalt mastics to simulate repeated environmental temperature variations. Dynamic shear rheological test (DSR) and atomic force microscopy test (AFM) were performed to characterize the evolution of the macroscopic rheological properties and microstructural characteristics under five cyclic temperature ranges. Pearson correlation analysis was utilized to explore the correlation between macro and micro properties. Following thermal cycling, it was observed that the two asphalt mastics experienced a decline in their viscous properties and became more elastic, resulting in a decrease in their stress relaxation capacity and asphalt-aggregate interaction on a macroscopic level. The microstructure transitioned from a multiphase to a homogeneous structure, while the expansion of the valley structure indicated the accumulation of microscopic defects. The larger the temperature variations and the higher the cyclic temperatures are, the more severe the deterioration in the viscoelasticity and microstructures of asphalt mastics is; the degradation of the micromechanical characteristics directly affects the macroscopic rheological properties. The bee structure ratio, the adhesion, and relaxation properties are sensitive to cyclic temperature variations and recommended to characterize the thermal cycling resistance. In comparison to 90# asphalt mastic, the SBS modified asphalt mastic exhibits great resistance to thermal deterioration. This study deepens the understanding of the causes of asphalt pavement performance deterioration in regions with frequent environmental temperature fluctuations.