Analysis of Temperature Stress and Temperature Fatigue Characteristics of Asphalt Mixtures
Yao Luo,Hao Wu,Yiqun Zhan
DOI: https://doi.org/10.2139/ssrn.4186643
2022-01-01
SSRN Electronic Journal
Abstract:Temperature cracking is one of the primary disease forms of asphalt pavements. The cracking of asphalt pavements caused by low temperature is rare. However, the problem of temperature fatigue damage caused by repeated changes in temperature is particularly pronounced and affects the service condition of pavement material and structure all the time. In this study, the mechanical behavior and damage characteristics of temperature fatigue for asphalt mixtures under temperature variation were systematically analyzed and discussed through tests and numerical analysis methods, quantifying the effects of monotonic and cyclic temperature variation on asphalt mixtures. Based on the modified temperature stress restrained specimen test (TSRST), the lowtemperature cracking test with the monotonic temperature variation and the temperature stress test in the cyclic temperature variation were carried out. Through theoretical analysis and calculation, the variation law of mechanical response of asphalt mixtures with temperature and time was obtained, the mechanical behavior of asphalt mixtures under the cyclic temperature variation was elucidated. Moreover, on the basis of testing results, the mechanical behavior of asphalt mixtures under different temperature ranges and different cooling rates was simulated and analyzed using the finite element method (FEM). The damage characteristics of temperature fatigue for asphalt mixtures under cyclic temperature variation during service life were revealed. The results of the study showed that: In the low-temperature cracking test, the temperature stress of asphalt mixtures increases non-linearly at a uniform cooling rate, using different cooling rates (10°C/h, 8°C/h, 6°C/h, 4°C/h, 2°C/h) for the simulation, it can be obtained that the faster the cooling rate, the larger the temperature stress generated. In the cyclic temperature stress test, due to the viscoelastic properties of asphalt mixtures, the temperature stress shows significant stress relaxation phenomena with temperature variation. The maximum values of temperature stress decrease gradually within each cycle. It revealed that under the same temperature variation, the temperature stress generated by the specimen decreases continuously. Through the simulation, it can be obtained that under different cooling ranges (-20°C to -10°C, -10°C to 0°C) and different cooling rates (10°C/h, 20°C/h), the temperature stress increases with the temperature range decrease. The temperature stress increases with the increase of the cooling rate, and the fatigue damage showed the same variation law. Different temperature ranges (-20 to 10°C, -10 to 0°C) and different pre-crack sizes (W10-H20 mm, W10-H10 mm, W5-H20 mm and W5H10 mm) were used to simulate the crack propagation by temperature cycle. The results showed that the lower the temperature range, the larger the stress intensity factor (K I ) generated. The faster crack propagation leads to the fewer number of temperature cycles. The pre-crack width has a lesser effect on the number of temperature cycles, while the pre-crack height has more influence.