Magnetocaloric Effects and Critical Behavior of La0.7Ca0.3−xSrxMnO3
Xiang Jin,Jing Zhao,HuaiJin Ma,Jianjun Zhao,Tegus O
DOI: https://doi.org/10.1007/s10948-024-06697-7
2024-02-20
Journal of Superconductivity and Novel Magnetism
Abstract:In this study, polycrystalline samples of La 0.7 Ca 0.3− x Sr x MnO 3 ( x = 0.00, 0.10, and 0.25) were prepared using the conventional solid-phase reaction method. The magnetocaloric effects and critical behavior of this series of polycrystalline materials were investigated. The research results indicate that all the samples are single-phase with an orthorhombic structure, belonging to the space group Pbnm. Under a magnetic field of 7 T, the maximum magnetic entropy changes of the samples were 9.74, 7.37, and 6.11 J·kg −1 ·K −1 , respectively, and the relative cooling power are 360.53, 361.04, and 366.50 J·kg −1 , respectively. The doped samples demonstrate superior magnetic refrigeration ability compared to the parent phase. It is noteworthy that the Curie temperature increases from 243 K ( x = 0.00) to 295 K ( x = 0.10) and 350 K ( x = 0.25). In addition, there is a transition from a first-order to a second-order phase transition in the sample with x = 0.25. The critical behavior of the compounds with x = 0.25 was analyzed using various methods, including modified Arrott plots, the Kouvel-Fisher method, and critical isotherm, to determine critical exponents ( β , γ , and δ ). The results obtained from both methods are close and indicate that the critical behavior of the sample crosses between mean field model and 3D-Heisenberg model. The temperature dependence of the order parameter n for different magnetic fields is studied using the relation |∆ S M |∝ H n . The values of n not only reveal the type of phase transition of the system but also validate the critical exponents. The results indicate that La 0.7 Ca 0.3− x Sr x MnO 3 ( x = 0.10, and 0.25) ceramics have the potential to be used as room-temperature magnetic refrigeration materials.
physics, condensed matter, applied