Abstract:We report the fabrication and catalytic performance evaluation of highly active and stable nickel (Ni)-based structured catalysts for ammonia dehydrogenation with nearly complete conversion using nonprecious metal catalysts. Low-temperature chemical alloying (LTCA) followed by selective aluminum (Al) dealloying was utilized to synthesize foam-type structured catalysts ready for implementation in commercial-scale catalytic reactors. The crystalline phases of Ni-Al alloy (NiAl3, Ni2Al3, or both) in the near-surface layer were controlled by tuning the alloying time. The best-performing catalyst was obtained from a Ni foam substrate with a NiAl3/Ni2Al3 overlayer synthesized by LTCA at 400 °C for 20 h. The developed Ni catalyst exhibited an activity enhancement of 10-fold over the nontreated Ni foam and showed outstanding activities of 15 800 molH2molNi-1h-1 (TOF: 4.39 s-1) and 19 978 molH2molNi-1h-1 (TOF: 5.55 s-1) at 550 and 600 °C, respectively. This performance is unprecedented compared with previously reported Ni-based ammonia cracking catalysts with higher-end performance (TOFs of 0.08-1.45 s-1 at 550 °C). Moreover, this catalyst showed excellent stability for 100 h at 600 °C while discharging an extremely low NH3 concentration of 1034 ppm. The NH3 concentration in the exhaust gas was further reduced to 690 and 271 ppm at 700 and 800 °C, respectively, while no deactivation was observed at these elevated temperatures. Through material characterizations, we clarified that controlling the degree of Al alloying in the outermost layer of Ni is a crucial factor in determining the activity and stability because residual Al possibly modifies the electronic structure of Ni for enhanced activity as well as transforming to acidic alumina for increased intrinsic activity and stability.

A New High Efficiency Catalyst of Co–Ni/CeO2 for Hydrogen Production by Ammonia Oxidative Decomposition at Low Temperature

Engineering MOx/Ni Inverse Catalysts for Low-Temperature CO2 Activation with High Methane Yields

Construction of Co/CeO2 catalyst and study on catalytic performance

Ce0.5Zr0.5O2 Solid Solutions Supported Co-Ni Catalyst for Ammonia Oxidative Decomposition to Hydrogen

Ce-promoted Ni-NiO Small Ensemble Constrained in an MgO Catalyst for Efficient Hydrogen Production Through NH3 Decomposition

Ce0.6Zr0.3Y0.1O2 solid solutions-supported Ni Co bimetal nanocatalysts for NH3 decomposition

Spatial Confinement of Electron-Rich Ni Nanoparticles for Efficient Ammonia Decomposition to Hydrogen Production

Promoted Multimetal Oxide Catalysts for the Generation of Hydrogen Via Ammonia Decomposition

Boosting hydrogen production of ammonia decomposition via the construction of metal-oxide interfaces

Highly active Ni/CeO2 catalyst for CO2 methanation: Preparation and characterization

Atomically Incorporating Ni into Mesoporous CeO2 Matrix via Synchronous Spray-Pyrolysis as Efficient Noble-Metal-Free Catalyst for Low-Temperature CO Oxidation

Hydrogen production from ammonia decomposition over Ni/CeO2 catalyst: Effect of CeO2 morphology

Ammonia Cracking Catalyzed by Ni Nanoparticles Confined in the Framework of CeO2 Support

Hydrogen Generation via Ammonia Decomposition on Highly Efficient and Stable Ru-free Catalysts: Approaching Complete Conversion at 450 oC

Facile Synthesis of Graphene-Supported Ni-CeO X Nanocomposites As Highly Efficient Catalysts for Hydrolytic Dehydrogenation of Ammonia Borane

Top-Down Syntheses of Nickel-Based Structured Catalysts for Hydrogen Production from Ammonia

Synergistic interface between metal Cu nanoparticles and CoO for highly efficient hydrogen production from ammonia borane

Highly active Ni/CeO2/SiO2 catalyst for low-temperature CO2 methanation: Synergistic effect of small Ni particles and optimal amount of CeO2

Monolithic microfibrous nickel catalyst co-modified with ceria and alumina for miniature hydrogen production via ammonia decomposition

Na‐ZSM‐5 Zeolite Nanocrystals Supported Nickel Nanoparticles for Efficient Hydrogen Production from Ammonia Decomposition

Catalyst Coatings for Ammonia Decomposition in Microchannels at High Temperature and Elevated Pressure for Use in Decentralized and Mobile Hydrogen Generation