Enhancing Comprehensive Performance of Crosslinked Pbi-Based High-Temperature Proton Exchange Membranes: Effectively Doping A Tetraphosphoric Acid Plasmonic Conductor

Xulei Zhi,Yanan Lv,Peng Sun,Ping Li,Hongchang Pei,Zhongfang Li

DOI: https://doi.org/10.2139/ssrn.4358402

2023-01-01

SSRN Electronic Journal

Abstract:The preparation of high temperature and low humidity proton exchange membranes with high proton conductivity is a subject of extensive research. The zirconium ethylenediamine tetramethylene phosphonate (ZrEDTMPS) proton conductor with –PO3H2 groups which can easily form hydrogen bonds and encourage proton transfer in low RH is synthesized and doped into the PBI-based membranes. The epoxy groups of tetrafunctional N, N, N’, N’-tetraglycidy-4,4'-diaminodiphenylmethane (TGDDM) react with the NH groups in polybenzimidazole and form a cross-linking network structure to improve the mechanical properties, oxidative stability and dimensional stability of the composite membranes. At 180°C, the proton conductivity of the mPBI-TGDDM(10%)/ZrEDTMPS(30%) is 0.122, 0.050 and 0.029 S cm-1 at 100%, 50% and 0 RH, respectively. Meanwhile, the mPBI-TGDDM/ZrEDTMPS membranes exhibit high oxidative stability (the mass loss of membranes is 2.1%). Compared with Nafion 117 (5.5×10−7 cm2 s−1), the methanol permeability of mPBI TGDDM/ZrEDTMPS composite membrane at 70 ° C (6.38×10-8 cm2 s-1) is one order of magnitude lower. The mPBI-TGDDM/ZrEDTMPS membranes have good comprehensive performance and can be used in proton exchange membrane fuel cells.