Resilient Si3N4@SiO2 Nanowire Aerogels for High-Temperature Electromagnetic Wave Transparency and Thermal Insulation

Wei Zhang,Lei Su,De Lu,Kang Peng,Min Niu,Lei Zhuan,Jian Feng,Hongjie Wang

DOI: https://doi.org/10.26599/jac.2023.9220813

IF: 11.534

2023-01-01

Journal of Advanced Ceramics

Abstract:With the development of aerospace technology, the Mach number of aircraft continues to increase, which puts forward higher performance requirements for high-temperature wave-transparent materials. Silicon nitrides have excellent mechanical properties, high-temperature stability, and oxidation resistance, but their brittleness and high dielectric constant impede their practical applications. Herein, by employing a template-assisted precursor pyrolysis method, we prepared a class of Si3N4@SiO2 nanowire aerogels (Si3N4@SiO2 NWAGs) that are assembled by Si3N4@SiO2 nanowires with diameters ranging from 386 to 631 nm. Si3N4@SiO2 NWAGs have low density of 12-31 mg.cm(-3), specific surface area of 4.13 m(2).g(-1), and average pore size of 68.9 mu m. Mechanical properties characterization shows that the aerogels exhibit reversible compressibility from 60% compressive strain and good fatigue resistance even when being compressed 100 times at set strain of 20%. The aerogels also show good thermal insulation performance (0.032 W.m(-1).K-1 at room temperature), ablation resistance (butane blow torch), and high-temperature stability (maximum service temperature in air over 1200.). The dielectric constant and loss of the aerogels are 1.02-1.06 and 4.3x10(-5)-1.4x10(-3) at room temperature, respectively. The combination of good mechanical, thermal, and dielectric properties makes Si3N4@SiO2 NWAGs promising ultralight wave-transparent and thermally insulating materials for applications at high temperatures.