Alternating Multilayered Si 3 N 4 /SiC Aerogels for Broadband and High-Temperature Electromagnetic Wave Absorption up to 1000 °C

Zhixin Cai,Lei Su,Hongjie Wang,Min Niu,Liting Tao,De Lu,Liang Xu,Mingzhu Li,Hongfei Gao
DOI: https://doi.org/10.1021/acsami.1c02906
2021-04-02
Abstract:Lightweight electromagnetic (EM) wave absorbers made of ceramics have sparked tremendous interest for applications in EM wave interference protection at high temperatures. However, EM wave absorption by pure ceramics still faces huge challenges due to the lack of efficient EM wave attenuation modes. Inspired by the energy dissipation mechanism during fracture of lobster shells with a soft and stiff multilayered structure, we fabricate a high-performance EM wave absorption ceramic aerogel composed of an alternating multilayered wave transparent Si<sub>3</sub>N<sub>4</sub> (N) layer and wave absorption SiC (C) layer by a simple restack method. The obtained N/C aerogel shows ultralow density (∼8 mg/cm<sup>3</sup>), broad effective absorption bandwidth (8.4 GHz), strong reflection loss (−45 dB) at room temperature, and excellent EM wave absorption performance at high temperatures up to 1000 °C. The attenuation of EM wave mainly results from a "reflection–absorption–zigzag reflection" process caused by the alternating multilayered structure. The superior absorption performance, especially at high temperatures, makes the N/C aerogel promising for next-generation wave absorption devices served in high-temperature environments.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c02906?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c02906</a>.The X-ray diffraction patterns of Si<sub>3</sub>N<sub>4</sub> and SiC aerogels; the SEM figures of Si<sub>3</sub>N<sub>4</sub> and SiC aerogels; the EM parameters and absorption performance of the N6/C6 aerogel at different temperatures, Tables showing comparison of comprehensive absorption performance of the N/C aerogel with other advanced microwave absorbing composites (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c02906/suppl_file/am1c02906_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to develop a lightweight material with broadband and efficient electromagnetic wave absorption performance in a high - temperature environment (up to 1000°C). Specifically, the researchers aim to overcome the challenges existing in electromagnetic wave absorption of pure ceramic materials, such as the lack of effective electromagnetic wave attenuation modes. ### Main Problems and Solutions 1. **Problems**: - Pure ceramic materials have deficiencies in electromagnetic wave absorption, especially in high - temperature environments. - It is necessary to develop a material that can maintain efficient electromagnetic wave absorption performance at high temperatures. 2. **Solutions**: - Inspired by the multi - layer structure of lobster shells, a Si₃N₄/SiC aerogel (N/C aerogel) with an alternating multi - layer structure was designed, in which the Si₃N₄ layer serves as a transparent layer and the SiC layer serves as an absorption layer. - Through this alternating multi - layer structure, the process of "reflection - absorption - zigzag reflection" is realized, thereby improving the attenuation efficiency of electromagnetic waves. ### Specific Implementation Methods - **Material Preparation**: SiC nanowires and Si₃N₄ nanoribbon aerogel papers were prepared by chemical vapor deposition respectively, and then assembled into alternating multi - layer structures with different numbers of layers by partial hot - pressing method. - **Performance Optimization**: The electromagnetic wave absorption performance of the material was optimized by adjusting the thickness and number of layers of Si₃N₄ and SiC layers. - **Experimental Verification**: The electromagnetic wave absorption performance of N/C aerogels with different numbers of layers was tested, and their stability and excellent performance in high - temperature environments were verified. ### Key Results - The N6/C6 aerogel exhibits the best electromagnetic wave absorption performance, with an effective absorption bandwidth of 8.4 GHz at room temperature and a minimum reflection loss of - 45 dB. - In a high - temperature environment (200°C to 1000°C), the N6/C6 aerogel can still maintain excellent electromagnetic wave absorption performance, covering the entire X - band. - The material has good thermal insulation performance and can maintain stable electromagnetic wave absorption characteristics even at a high temperature of 1000°C. ### Conclusion By designing the Si₃N₄/SiC aerogel with an alternating multi - layer structure, the researchers have successfully developed a lightweight, high - temperature - resistant material with excellent electromagnetic wave absorption performance, which is suitable for electromagnetic wave interference protection in high - temperature environments, especially for the protection of electronic devices under extreme conditions.