Abstract:Harnessing their excellent physical attributes, two-dimensional nanostructures have gained prominences as re-inforcements in polymer nanocomposites. Given the intricate structure of nanofillers and the varied interfacial connections, in-depth understanding of the strengthening mechanisms becomes pivotal for optimizing nano-composite design. By varying the GO's morphology, a notable divergence of approximately 30% is evident in the interfacial shear strength. This divergence is attributed to the mechanical interlocking effect instigated by the presence of -O-and-OH functional groups. Functionalizing with groups like-CH3-CH2-NH2 (-Ethylamine) and-(HOCH2)3CNH2 (-TRIS) enhances the mass density of PE polymers at the interphase, which changes the interface sliding (low-density interphase) to the cohesive sliding during the pull-out process. As a result, the maximum interfacial shear strength (204-223 MPa) of these two samples is much larger than that of the pristine GO/PE (149-151 MPa), and even comparable with the pure PE's tensile strength. Intriguingly, shorter or highly flexible functional group exhibit a comparatively weaker influence on the interfacial shear strength. Moreover, as the sliding surface shifts toward the cohesive zone, diminishing sample thickness (less than 60 angstrom) generally corre-sponds to augmented interfacial shear strength due to the boundary confinement effect. In summary, this work offers a comprehensively elucidation of GO/PE pull-out behavior, facilitating the design of nanocomposites with exceptional mechanical performance.

Sliding Behavior at the Graphene Oxide and Polyethylene Interface