Rapid Solid-State Thermal Diffusion Fabrication of Mg-Zn Intermetallic Layer for Hardening Surface and Improving Corrosion Resistance of AZ31 Alloy

Yi Lin,Xianwei Fu,Qiang Zhong,Zhengbing Xu,Jun Tan

DOI: https://doi.org/10.1016/j.surfcoat.2024.131017

IF: 4.865

2024-01-01

Surface and Coatings Technology

Abstract:The Mg–Zn intermetallic layer for strengthening the surface of AZ31 alloy was fabricated by solid–state thermal diffusion with pressure at different temperatures. Microstructure evolution of Mg–Zn intermetallic layer during the fabrication process was observed by X–ray diffraction, optical microscopy, and scanning electron microscopy. As a result, the maximum fabrication rate of Mg–Zn thermal diffusion layer could reach 3×103 μmꞏh-1, and most of obtained Mg–Zn intermetallic layers in the surface of samples could be divided into three layers according to the type of components, namely internal diffusion layer, middle diffusion layer, and outer diffusion layer. The internal diffusion layer was mainly composed of Mg7Zn3 phase, the middle diffusion layer consisted of MgZn and α–Mg phases, and the outer diffusion layer was predominated by MgZn2 phase. The generation of MgZn phases mainly derived from the eutectoid transformation of Mg7Zn3 phase and the melting crystal transformation of Mg2Zn3 phase in the thermal diffusion process. Furthermore, the formation of the Mg–Zn intermetallic layer effectively improved the microhardness and corrosion resistance of the AZ31 alloy. Especially, when the thermal diffusion was conducted at 360°C for 54 min under 10 MPa, not only the surface microhardness of obtained sample was up to 3.6 times that of AZ31 alloy, but also the corrosion current was reduced by about one order of magnitude. However, as the sample was subjected to thermal diffusion at a higher temperature and pressure (e.g., 400°C@30MPa), the deterioration would bring out the microhardness and corrosion resistance, ascribing from the formation of α–Mg phases with softer texture and more negative potential along the grain boundaries of MgZn phases.