Abstract:Exploration of efficient deep red phosphor based on non-rare-earth ion activated oxide is of great practical value in the field of phosphors converted white light-emitting diode lighting. A spinel Mg1+yAl2-xO4:xMn(4+), yMg(2+) phosphor with deep red emission is synthesized by a solid-state reaction route. The crystal structure and morphology are characterized by powder X-ray diffraction and scanning electron microscopy. The luminescent performance is characterized by fluorescence spectrophotometer and fluorescence decay curves. The results demonstrate that the synthesized phosphor shows that two excited spectrum bands centered at 290 nm and 438 nm cover a broad spectral region from 220 nm to 500 nm due to the Mn4+-O2- charge transfer band and the (4)A(2)-T-4(1) and T-4(2) transitions of Mn4+ ions. Upon excitation at 300 nm, a strong, narrow red emission band is observed between 600 and 700 nm peaked at 652 nm as a result of the spin-forbidden E-2(g)-(4)A(2g) electron transition of Mn4+. The corresponding chromaticity coordinate is (0.7256, 0.2854). Additionally, the concentration quenching of Mn4+ in the MgAl2O4 host is evaluated in detail, which indicates that the optimum doping concentration of Mn4+ is experimentally determined to be 0.14 mol%. The critical distance is calculated to be 52.15 angstrom according to the Blasse equation, which elucidates that the concentration quenching mechanism is consequently very likely to be induced by the multipole-multipole interaction. The crystal field strength (D-q) and the Racah parameters (B and C) are estimated to evaluate the nephelauxetic effect of Mn4+ suffered in MgAl2O4:Mn4+ host lattice. Luminous mechanism is explained by Tanabe-Sugano energy level diagram of Mn4+ ion. The ratio of Dq/B equals 1.74, indicating that Mn4+ ions experience a weak crystal field in the MgAl2O4 host and emission peak energy of E-2(g)-(4)A(2g) transition is dependent on the nephelauxetic effect. The red emission intensity of Mg1+yAl2-xO4:xMn(4+), yMg(2+) increases on account of excess Mg2+ which would compensate for the local charge balance surrounding Mn4+ ions, furthermore, lead the Mn4+-Mn4+ pairs connected with interstitial O2- to transform into isolated Mn4+ ions, and thus eliminating energy transfer and enhancing the luminescence efficiency effectively. The decay times of two time-dependent curves of Mg1+yAl2-xO4:xMn(4+), yMg(2+) are 0.672 ms and 0.604 ms, and each entire decay curve could be well-fitted to single-exponential, confirming that there is only a single Mn4+ ion luminescence center. The decay time of Mn 4 + luminescence is prolonged with the increase of Mg2+ content, indicating that excitation energy transfer and non-radiative relaxation between Mn4+-Mn4+ pairs decrease, the reason is that photoexcitation energy can be temporarily stored in the trapping centers induced by excess positive charges. These results imply that Mn4+ doped Mg1+yAl2-xO4:xMn(4+), yMg(2+) is a promising candidate of deep-red phosphors for near-UV and blue light emitting diodes. These findings in the paper would be beneficial not only to developing a low-cost and safe strategy to produce high-efficient Mn4+ activated luminescent materials for white light emitting diodes, but also to providing a new insight into improving the photoluminescence properties of Mn4+.

The Effect of Li+ on Structures and Luminescence Properties of Znal2o4: Mn2+(Mn4+), Li+ Phosphors

Adjusting luminescence properties of ZnAl2O4:Mn2+(Mn4+), Li+ phosphors through cation substitution

Insight into a Novel Rare-Earth-free Red-Emitting Phosphor Li3Mg2NbO6:Mn4+: Structure and Luminescence Properties

Localized Charge Accumulation Driven by Li + Incorporation for Efficient LED Phosphors with Tunable Photoluminescence

The Effect of Co-Doping Ions on the Luminescence Properties and Energy Transfer of Ba1.8-3x/2-y-zZnzLi0.4SiO4:xCe3+,yMn2+ Phosphors

Analysis of the Structure and Abnormal Photoluminescence of a Red-Emitting LiMgBO3:Mn2+ Phosphor.

Charge Compensating Effect of Cation Doping on the Enhanced Luminescent and Stability of La2LiTaO6:Mn4+ Red Phosphor

Site Occupancy Preference, Enhancement Mechanism, and Thermal Resistance of Mn4+ Red Luminescence in Sr4al14o25: Mn4+ for Warm Wleds

Effect of Alkali Metal Ions (Li+, Na+ and K+) on the Luminescent Properties of ZnTiO3: Eu3+ Phosphors

Enhanced Luminescence Performances of Mn4+:Y3Al5O12 Red Phosphor by Ions of Rn2+ (be2+, Mg2+, Sr2+, Ba2+)

Unveiling luminescence property of Li 2 MgGeO 4 :Mn 4+ featuring tetrahedral crystallographic-site occupancy of Mn 4+

Effects of Na+, Ga3+ introduction on the luminescence properties of LiAl4O6F: Mn4+ red fluorescent materials

Synthesis and Luminescence Properties of a Novel Deep Red Phosphor Li2ZnTi3O8:Mn4+ for Plant-Cultivation.

Enhanced Luminescence Performances of Tunable Lu3-xYxAl5O12:Mn4+ Red Phosphor by Ions of Rn+ (Li+, Na+, Ca2+, Mg2+, Sr2+, Sc3+)

Preparation of Mg1+yAl2-xO4:xMn(4+), yMg(2+) deep red phosphor and their optical properties

Effect of Zn2+ and Li+ codoping ions on nanosized Gd2O3:Eu3+ phosphor

Effect of Li+ and Zn2+ Co-doping on Luminescent Properties of Gd2O3:Eu3+ Nanoparticles

Novel Non-Rare-earth Red-Emitting Phosphor Li4AlSbO6:Mn4+ for Plant Growth: Crystal Structure, Luminescence Properties and Its LED Device

Enhancing Luminescence of Lu2MoO6:Eu3+ Phosphors by Doping with Li+ Ions for Near Ultraviolet Based Solid State Lighting

The effect of electron cloud expansion on the red luminescence of Sr 4 Al 14 O 25 :Mn 4+ revealed by calculation of the Racah parameters

Structural Confinement Toward Giant Enhancement Of Red Emission In Mn2+-Based Phosphors