Abstract:Abstract The synthesis of ambient-cured sustainable geopolymer mortars (GMs) was studied throughout this work. To reduce carbon dioxide emissions, new materials must be used in the production of sustainable concrete and mortars. Many types of binders are used in the synthesis of GM and concrete (GPC), especially clay minerals. These clay minerals are considered sources of alumina and silica in GM and concrete. The geopolymerization process relies on the alkaline solution activating the alumino-silicate to produce geopolymer gel products. The palygorskite (PA) clay mineral, sodium hydroxide (NaOH), and sodium silicates (Na 2 SiO 3 ) were chosen as a binder (solid material) and alkaline activator solution to synthesize GM at ambient temperature. PA was thermally treated at 550, 650, 700, and 750°C, respectively, to convert into high-reactive PA (HRP) HRP550, HRP650, HRP700, and HRP750, respectively. The characteristics of PA clay, HRP powders, and HRP-based GM were evaluated using compressive strength (CS) testing, X-ray fluorescence analysis, c arbon footprint analysis, X-ray diffraction (XRD) diffractograms, Fourier transform infrared spectroscopy (FTIR) spectroscopy, scanning electron microscopy (SEM) images, and energy-dispersive X-ray spectroscopy (EDS) analysis. The maximum CS of 25.1 MPa was acquired for geopolymer synthesis utilizing HRP700-based GM cured at 30°C for 28 days. FTIR spectroscopy demonstrated that HRP-based GM showed the presence of Si–O, Al–O, and O–C–O bonds stretching vibrations in the alumino-silicate network. The results showed that the CO 2 emissions had a reduction in the HRP-based GM compared with the reference mix of ordinary Portland cement mortar (OPM). The percentage of reductions was 14.1, 13.7, 13.1, and 12.4 for HRP550, HRP650, HRP700, and HRP750, respectively, compared with the OPM mixture. SEM images/EDS analysis and XRD diffractograms confirmed the presence of sodium alumino-silicate hydrates, magnesium silicate hydrate, and calcium silicate hydrate gels with high quantities particularly in the HRP700-based GM than that in HRP550, HRP650, and HRP750, respectively. The results indicate the suitability of HRP calcined at 700°C (HRP700) in the synthesis of the GM.

Preparation of One-Part Geopolymer Based on Thermally Activated Soda Residue

Performance Characteristics of Micro Fiber-Reinforced Ambient Cured One-Part Geopolymer Mortar for Repairing

Alkali-hydrothermal activation of mine tailings to prepare one-part geopolymer: Activation mechanism, workability, strength, and hydration reaction

Synthesis, characterization and mechanisms of one-part geopolymeric cement by calcining low-quality kaolin with alkali

Enhancing solidification in one-part geopolymer systems through alkali-thermal activation of bauxite residue and silica fume integration

Recovered soda residue as alkaline activator of furnace slag: geopolymer prepared from furnace slag incorporated with soda residue and its reuse in composite cement

Sulphate resistance of one-part geopolymer synthesized by calcium carbide residue-sodium carbonate-activation of slag

The Effect of Superplasticizers on Eco-friendly Low-Energy One-Part Alkali-Activated Slag

Development of high strength one-part geopolymer mortar using sodium metasilicate

A Prefatory Sustainability Assessment of One-Part Geopolymers

Preparation and Characterization of Low-Carbon Cementitious Materials Based on Soda-Residue-Activated Ground Granulated Blast-Furnace Slag: A Case Study on Cemented Paste Backfills

Synthesis of one-part geopolymers from alkaline-activated molybdenum tailings: Mechanical properties and microstructural evolution

Properties and Hydration Mechanism of Soda Residue-Activated Ground Granulated Blast Furnace Slag Cementitious Materials

Effects of silicate modulus and alkali dosage on the performance of one-part electric furnace nickel slag-based geopolymer repair materials

Optimization and characterization of sustainable geopolymer mortars based on palygorskite clay, water glass, and sodium hydroxide

Effect of Na + alkaline activation on the geopolymerization of a pure metakaolin at room temperature

Mechanical and microstructural properties of one-part geopolymer-solidified soil attacked by Na 2 SO 4

Utilizing Raw Phosphogypsum to Prepare One-Part Geopolymer: Mechanical Properties, Optimization, and Hydration Mechanisms

Effects of Spodumene Flotation Tailings on Mechanical Properties of Acid-Based Geopolymer Mortar

Acid-resistance of one-part geopolymers: Sodium aluminate and carbonate as alternative activators to conventional sodium metasilicate and hydroxide

Study on the Compressive Strength and Reaction Mechanism of Alkali-Activated Geopolymer Materials Using Coal Gangue and Ground Granulated Blast Furnace Slag