Abstract:The 2195 Al-Cu-Li alloy is widely utilized in the aerospace industry due to its lightweight nature and high strength. Consequently, gaining a comprehensive understanding of techniques to enhance its microstructural and mechanical properties is crucial for the consistent production of reliable and high-strength aerospace components. In this investigation, a pristine 2195 industrial ingot was subject to three distinct forging pretreatments: PT1, which involved a direct three upsetting and three stretching (3U3S) process; PT2, which combined double stage homogenization (DH) with 3U3S; and PT3, which involved DH along with six upsetting and six stretching (6U6S). Subsequent warm deformation and T8 aging treatment were applied to the pretreated forgings. The microstructure evolution during the processes and the final mechanical properties in three orthogonal dimensions were examined. The findings revealed that the combination of DH and multi-dimensional forging (MDF) facilitated the dissolution of non-equilibrium phases to a greater extent. Consequently, the main strengthening phase transformed from the T 1 + δ` phase observed in PT1 to the denser T1 + little θ` phase observed in PT2 and PT3 after T8 aging treatment. Notably, the tensile strength and yield strength of PT2 and PT3 specimens increased by 20-30 MPa in all three directions. Moreover, the MDF process accelerated the recrystallization behavior from PT1 to PT3, resulting in a gradual reduction in the average grain size of the pretreated samples from 356 μm to 186 μm. Following warm forging and T8 aging, the grains exhibited a finer and equiaxed structure. Additionally, the coarse phase was identified as the primary source of transgranular cracking. The coarse phases within the matrix became more homogeneous and finer from PT1 to PT3, with a gradual decrease in their area fraction. On the fracture surfaces, the aggregation of coarse phases diminished. Consequently, the elongation in the z-direction improved, and the elongation anisotropy and standard deviation decreased in all three directions for PT3 specimens. The findings presented in this study provide valuable insights into the high-performance manufacturing of Al-Cu-Li alloys.

Microstructure and Mechanical Properties of Al–Li Alloy Manufactured by Additive Friction Stir Deposition

Effect of Heat Treatment States of Feedstock on the Microstructure and Mechanical Properties of AA2219 Layers Deposited by Additive Friction Stir Deposition

Microstructural Characterization and Mechanical Properties of AlMg Alloy Fabricated by Additive Friction Stir Deposition

Microstructural evolution and mechanical properties of the rapidly-solidified and hot-extruded 2196 Al-Li alloy

The effect of heat treatment on the microstructure and electrochemical corrosion behavior of multilayer AA6061 alloy fabricated by additive friction stir deposition

Quantitative study on the correlation between microstructure and mechanical properties of additive friction stir deposited

Microstructures and mechanical properties of a cast Al–Cu–Li alloy during heat treatment procedure

Effect of forging pretreatment on the microstructures and mechanical properties of the Al-Cu-Li alloy

Effect of Rotational Shear and Heat Input on the Microstructure and Mechanical Properties of Large-Diameter 6061 Aluminium Alloy Additive Friction Stir Deposition

Microstructure, mechanical and fracture properties of friction stir welded 2195 Al-Li alloy joints

Enhanced matrix precipitation of T1 (Al2CuLi) phase in AA2055 Al–Li alloy during stress aging process

Microstructures and Mechanical Properties of Al-Li Alloy Friction Stir Weld

Additive friction stir deposition of al 7075 parts and the effect of heat treatment on microstructure, electroconductivity, and mechanical properties

Effect of Heat Treatment on the Microstructure and Mechanical Properties of Extruded Al–4Cu–1Li–0.4Mg–0.4Ag–0.18Zr Alloy

Microstructure Evolution and Mechanical Properties of Friction Stir Welded Al–Cu–Li Alloy

Comprehensive Understanding of the Mechanical Properties and Microstructure Evolution of Aluminum Alloy/steel Laminates During Friction Stir-Assisted Incremental Forming with Synchronous Bonding Process

Effect of Li addition on microstructure and mechanical properties of Al – Mg – Si alloy

Microstructure and Mechanical Properties of Cast Al-Li-Mg Alloy: Role of Cu Addition and Heat Treatment

Microstructure characteristics of an ultra-high strength extruded Al-4.7Cu–1Li-0.5Mg-0.1Zr–1Zn alloy during heat treatment

Room Temperature Strengthening and High-Temperature Superplasticity of Mg-Li-Al-Sr-Y Alloy Fabricated by Asymmetric Rolling and Friction Stir Processing

Improving joint performance of friction stir welded 2195-O Al–Li alloy by post-weld heat treatment and rolling deformation