Abstract:We report on the formation of rutile TiO2 flocculent laser-induced periodic surface structures (LIPSSs) with high antireflectivity and superhydrophobicity on the surface of titanium under 10 ns 1064 nm laser irradiation without focusing. The center part of the Gaussian laser beam is used to deposit flocculent structure and the edge part used to produce LIPSSs. The melt and modification thresholds of titanium were determined first, and then, the melt and modification spot-overlap numbers, several responsible for the formation of flocculent structure and LIPSSs, were introduced. It is found that both the melt and modification spot-overlap numbers increase with an increase in laser fluence and spot-overlap number, contributing to the production of flocculent LIPSSs. LIPSSs are obtained with the modification spot-overlap number above 300, and the amount of flocculent structures increases with an increase in the peak laser fluence and spot-overlap number. Then, considering that the fine adjustment of the melt and modification spot-overlop numbers in one-time line scanning is quite difficult, the composite structure, of which both LIPSSs and flocculent structures are distinct, was optimized using laser line scanning twice. On this basis, a characterization test shows the sample full of the flocculent LIPSSs represents best antireflectivity with the value around 10% in the waveband between 260 and 2600 nm (advance 5 times in infrared wavelengths compared to the initial titanium surface), and shows the no-stick hydrophobicity with the contact angle of 160° and roll-off angle of 25° because of the pure rutile phase of TiO2.

Quasi Two-Dimensional Electron Gas Generated by Laser Irradiation at Rutile TiO <sub>2</sub> Surface

Quasi two-dimensional electron gas generated by laser irradiation at rutile TiO2 surface

Two-Dimensional Electronic Transport at the Bare KTaO 3 (100) Single Crystals by Laser Irradiation

Magnetic Conductive Outer Layer in Oxygen‐Deficient TiO 2 Single Crystals

Creation and Modulation of Conductivity in Laser-Irradiated SrTiO3 Single Crystals

Orientation-Dependent Crack Patterns at the Surface of Srtio3 Crystals Induced by Laser Irradiation

Oxygen Vacancy-Induced Room Temperature Ferromagnetism in Rutile TiO2

Coexistence of Both Localized Electronic States and Electron Gas at Rutile TiO2 Surfaces

Electron Irradiation Induced Room Temperature Ferromagnetism in Single Crystal TiO2 Substrate

Femtosecond Laser Direct Writing of TiO 2 Crystalline Patterns in Glass

Identification of surface oxygen vacancy-related phonon–plasmon coupling in TiO2 single crystal*

Periodic structure with a periodicity of 2–3.5 μm on crystalline TiO 2 induced by unpolarized KrF excimer lasers

Optical Properties of Pulsed Laser Deposited Rutile Titanium Dioxide Films on Quartz Substrates Determined by Raman Scattering and Transmittance Spectra

Direct In-Situ Insights into the Asymmetric Surface Reconstruction of Rutile TiO2 (110)

Formation of 100-nm periodic structures on a titanium surface by exploiting the oxidation and third harmonic generation induced by femtosecond laser pulses.

Laser irradiation induced structural transformation in layered transition metal trichalcogenide nanoflakes

Rutile TiO2 Flocculent Ripples with High Antireflectivity and Superhydrophobicity on the Surface of Titanium under 10 ns Laser Irradiation without Focusing.

Electronic relaxation in PLD TiO 2 films processed with femtosecond UV-laser

Direct in-situ insights into the asymmetric surface reconstruction of rutile TiO 2 (110)

Laser induced surface magnetization in Floquet-Weyl semimetals

Direct in Situ Determination and Modulation of Asymmetric Surface Reconstruction on Rutile TiO2

Quasi Two-Dimensional Electron Gas Generated by Laser Irradiation at Rutile TiO &lt;sub&gt;2&lt;/sub&gt; Surface