Thin-Film Composite Membrane Prepared by Interfacial Polymerization on the Integrated ZIF-L Nanosheets Interface for Pervaporation Dehydration
Xin Zhang,Zi-Ming Zhan,Feng-Yi Cheng,Zhen-Liang Xu,Peng-Rui Jin,Ze-Peng Liu,Xiao-Hua Ma,Xin-Ru Xu,Bart Van der Bruggen
DOI: https://doi.org/10.1021/acsami.1c09221
2021-08-10
Abstract:Thin-film composite (TFC) membranes are attracting wide attention because their ultrathin selective layer usually corresponds to the higher membrane flux for pervaporation. However, the direct preparation of the TFC membranes on ceramic substrates confronted with the great difficulties because the larger pores on ceramic substrate surfaces are detrimental to the formation of an intact polyamide (PA) selective layer produced by interfacial polymerization (IP) reaction. Here, the integrated ZIF-L nanosheets were proposed to be used as an assistance interlayer for the first time to eliminate the existence of the pores of the ceramic support, and provides a better basis for the formation of an intact PA selective layer by IP reaction between TMC and ethylenediamine (EDA). The experimental data obtained in pervaporation (PV) show that the increased flux from 1.1 to 2.9 kg/m2h corresponds to the decreased separation factor from 396 to 110 when the feed concentration of ethanol decreases from 95 wt % to 80 wt % at 50 °C. In addition, the membrane flux increases from 0.8 to 2.5 kg/m2h with a change of the separation factor from 683 to 111 when the operational temperature varies from 30 to 60 °C. These results demonstrate the great potential of the fabricated TFC membranes in practical application for PV dehydration of organic solutions.(PDF) The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c09221.Figure S1, schematic diagram of vacuum filtration process; Figure S2, schematic diagram of vacuum filtration process for removing redundant EDA solution; Figure S3, SEM images and XRD patterns of alumina support with ZIF-L nanosheets in ref 34; Figure S4, X-ray diffraction patterns of the ZIF-L nanosheet on the ceramic support without (and with) 1.0 wt % EDA treatment; Figure S5, surface and cross-section images of the ceramic support with EDA treated ZIF-L nanosheets; Figure S6, IP mechanism of the PA layer produced by the reaction between EDA and TMC; Table S1, comparison of separation performance of the TFC membranes for the dehydration of ethanol–water mixtures (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology