Abstract:As a promising replacement for nitride red phosphors, Ce: Y3(Mg1.8Al1.4Si1.8)O12(Ce: YMASG) ceramic phosphors have attracted significant attention recently for their advantages in inorganic encapsulation and massive red‐shifting of Ce3+ emission. In this work, Ce: YMASG with different doping concentrations of Ce3+ and Al2O3, was fabricated by vacuum sintering to investigate its effects on the elimination of the impurity phase and the enhancement of the luminescent properties of white light‐emitting diodes (w‐LEDs). It was discovered that the emission wavelength redshifts from 592 nm to 606 nm as the Ce3+ concentration increases, while at 450 K, the emission intensity deteriorates from 0.47 to 0.36 of its initial value. The Rietveld analysis revealed the presence of an impurity phase of Y4MgSi3O13 with a concentration of 17.021 wt% in Ce: YMASG. With the introduction of Al2O3, the impurity phase was eliminated from the matrix completely, the emission peak shifted to a shorter wavelength, and the thermal stability was greatly improved. When the correlated color temperature was controlled at around 3000 K in the packaged w‐LEDs, the commission international de l'éclairage (CIE) chromaticity coordinates shifted toward the bottom left corner of the diagram with increasing concentration of Ce3+. Conversely, the luminous efficiency (LE) increased from 36 lm/W to 58.6 lm/W as the concentration of Al2O3 increased from 0 to 10 wt%, which demonstrated the application prospect of the fabricated phosphor in warm w‐LEDs.

Dye-embedded YAG:Ce<sup>3+</sup>@SiO<sub>2</sub>composite phosphors toward warm wLEDs through radiative energy transfer: preparation, characterization and luminescence properties

White LED Based on YAG : Ce,Gd Phosphor and CdSe–ZnS Core/Shell Quantum Dots

Luminescence Properties And Energy Transfer Of Ce3+,Tb3+-Coactivated-Sialon Phosphors

Correction: Dye-embedded YAG:Ce 3+ @SiO 2 composite phosphors toward warm wLEDs through radiative energy transfer: preparation, characterization and luminescence properties.

Massive Red-Shifting of Ce3+ Emission by Mg2+ and Si4+ Doping of YAG:Ce Transparent Ceramic Phosphors

An orange-yellow-emitting Lu<sub>2-<i>x</i></sub>Mg<sub>2</sub>Al<sub>2-<i>y</i></sub>Ga<sub><i>y< /i></sub>Si<sub>2</sub>O<sub>12</sub>:<i>x</i>Ce<SUP>3+</SUP> phosphor-in-glass film for laser-driven white light

Synthesis, crystal structure and luminescence properties of a Y4Si2O7N2:Ce3+ phosphor for near-UV white LEDs

Optimization of Ce 3+ concentration and Y 4 MgSi 3 O 13 phase in Mg 2+ ‐Si 4+ Co‐doped Ce: YAG ceramic phosphors

Tunable luminescence Y3Al5O12:0.06Ce 3+, xMn2+ phosphors with different charge compensators for warm white light emitting diodes

Simulation of optical behavior of YAG:Ce3+@SiO2 phosphor used for chip scale packages WLED

Fabrication of ternary ZrO2-Al2O3-YAG:Ce ceramic phosphors for white light-emitting diodes

The application YAG:Ce3+@SiO2 phosphor for improving color deviation of phosphor-converted light-emitting diode

Tunable luminescence Y_3Al_5O_12:006Ce^3+, xMn^2+ phosphors with different charge compensators for warm white light emitting diodes

Crystal Structure and Photo-Luminescence of Gd3Ga2(Al3-ySiy)(O12-yNy):Ce3+ Phosphors for AC-warm LEDS

Correction: Dye-embedded YAG:Ce3+@SiO2 composite phosphors toward warm wLEDs through radiative energy transfer: preparation, characterization and luminescence properties

(Sr, Ca)AlSiN3:Eu2+ Phosphor-Doped YAG:Ce3+ Transparent Ceramics as Novel Green-Light-Emitting Materials for White LEDs

Red Emission Generation in Ce3+/Mn2+ Co-Doping Y3Al5O12 Phosphor Ceramics for Warm White Lighting Emitting Diodes

Energy transfer and thermal stability enhancement in Ce/Cr co-doped Al 2 O 3 /YAG eutectic phosphor ceramics for broadband red-emission

High‐Efficiency Cyan–Green‐Emitting Y3Sc2Ga3O12:Ce Phosphor for Microcrystals and Ultrathin Phosphor‐Glass Composite for Light‐Emitting Diode

Highly crystalline Y3Al5O12:Ce3+ phosphor-in-silica glass ceramics for high-power solid-state lighting

Crystallization and Fluorescence Properties of Ce:Yag Glass-Ceramics with Low Sio2 Content