Abstract:Ti6Al4V (TC4) alloy has been widely applied in the military, industrial, chemical, and medical fields due to their excellent thermal stability, corrosion resistance , and biocompatibility. However, titanium alloys are notorious for their poor tribological properties, such as their high friction coefficients and low surface bearing capacities. To tackle this problem, combination of laser surface texturing (LST) and double glow plasma chromizing was conducted to improve the wear resistance of TC4. LST was first conducted to produce uniform dimples with a diameter of 300 μm and gradient density of 11 % on the Ti6Al4V substrate. A chromizing coating (Cr-coating) was subsequently deposited on the surfaces of the textured and raw Ti6Al4V alloy by double glow plasma surface alloying (DGPSA). A continuous and compact Cr-coating with a thickness of about 55 μm was formed on TC4 after being maintained at a temperature of 850 °C, and the coating was mainly composed of a solid solution and intermetallic compounds of Cr 2 Ti phases. The surface hardness after alloying was two times higher than that of the TC4 substrate. Comparative assessments on the wear resistance of the Cr-coatings with and without LST treatment and the TC4 alloy were carried out using a ball-on-disk wear tester. The results showed that the mass loss and specific wear rate of the duplex-treated sample were 1.54 mg and 7.14 × 10 −4 mm 3 ·N −1 ·m −1 . The mass loss and specific wear rate of the TC4 were 4.32 mg and 1.62 × 10 −3 mm 3 ·N −1 ·m −1 . The specific wear rates of the four tested samples were in the following order: the duplex-treated TC4 < textured TC4 < chromized TC4 < polished TC4. The coating obtained by LST-double glow plasma chromizing duplex treatment exhibited an outstanding durability and the best mechanical performance. Thus, this approach be used for the protection of Ti6Al4V surface in engineering components and medical instruments.

Laser-surface Alloying of a Titanium Aluminide Alloy for Al 2 O 3 /tial Wear-Resistant Composite Coatings

Microstructure and Wear Resistance of a Laser Surface Alloyed γ-TiAl Intermetallic Alloy Ti-48Al-2Cr-2Nb

Microstructure and Tribological Properties of Laser Surface Alloyed TiN and TiC Reinforced Composite Coatings on TiAl Intermetallic Alloy

Microstructure and high-temperature wear resistance of a laser surface alloyed γ-TiAl with carbon

Wear and Oxidation Resistance Coatings Fabricated on Ti-6al-4v by Laser Surface Alloying Technique

Microstructure, wear and high-temperature oxidation resistance of laser clad Ti5Si3/γ/TiSi composite coatings on γ-TiAl intermetallic alloy

Microstructure and Properties of Laser Surface Alloyed γ-NiCrAl/TiC/Cr7C3 Composite Coatings on γ-TiAl Intermetallic Alloy

Wear-resistant Ti 5Si 3/Ti composite coatings made by laser surface alloying

MICROSTRUCTURE AND TRIBOLOGICAL PROPERTIES OF A LASER SURFACE ALLOYED Γ-Tial INTERMETALLIC ALLOY

In-situ TiB2-TiC reinforced Fe-Al composite coating on 6061 aluminum alloy by laser surface modification

Wear Resistance of a Laser Surface Alloyed Ti–6Al–4V Alloy

Microstructure and Wear Resistance of Ti5Si3/Ti3Al Composite Coatings Prepared by Laser Cladding on TA2 Titanium Alloy

Laser Surface Alloying of Pure Titanium with TiN–B–Si–Ni Mixed Powders

Microstructure and Wear Resistance of a Composite Coating Prepared by Laser Alloying with Ni-Coated Graphite on Ti-6Al-4V Alloy

Microstructure and Properties of Laser Cladding TiC/TiAl Composite Coatings on Γ-Tial Intermetallic Alloy

Combining laser surface texturing and double glow plasma surface chromizing to improve tribological performance of Ti6Al4V alloy

Study on Wear Resistance of Laser Clad Composite Coatings on TiAl Intermetallic Alloy

Study on Wear Resistance of Ti-6Al-4V Alloy Composite Coating Prepared by Laser Alloying

Development and Characterization of Laser Clad High Temperature Self-Lubricating Wear Resistant Composite Coatings on Ti–6Al–4V Alloy

Laser Synthesis of Titanium Aluminides Matrix Composite Coatings Reinforced by In-Situ Titanium Carbide Particles on Ti-6Al-4V Substrate

Microstructure and tribological properties of laser in-situ synthesized Ti3Al composite coating on Ti-6Al-4V