Abstract:Kinetics of cristobalite precipitation in a binary glass composite, containing a low-softening borosilicate (BSG) and a high-softening high silica (HSG) glass, have been investigated. XRD results show that the pure glasses do not crystallize under the sintering conditions used, but when mixed in appropriate proportions the cristobalite gradually precipitates out of the initial amorphous binary glass mixture as the sintering continues at temperatures ranging from 800 to 1000-degrees-C. Average linear thermal expansion coefficient (TCE) results show that the TCE increases significantly with increasing precipitation of cristobalite as a function of sintering time. Comparing the experimental TCE results with those theoretically calculated, it is concluded that the precipitation originates most likely in the HSG rather than in the BSG. The precipitation kinetics follow the Avrami equation, and the results show an apparent activation energy of 82 kJ/mol which is close to those for the diffusion of alkali ions in silicate glasses, suggesting mass-transport controlled kinetics. The values of the Avrami exponent are 1.7-1.8, which could be interpreted as a 3-dimension diffusional growth at zero nucleation rate. The linear growth rates of cristobalite, calculated from the precipitation curve, are in the range of 4-8 X 10(-5) mum/min, and show slight temperature dependence from 800 to 1000-degrees-C. The linear growth rates of cristobalite are also calculated theoretically using the equation derived by Turnbull et al.,2 and the data are 0-3 orders of magnitude smaller than those observed experimentally. This disparity is attributed to the catalytic effect of the OH and O in air and in the glass network, as well as the diffusion of alkali ions from BSG to HSG.

Crystal Growth Inhibitor in Binary Borosilicate Glass Composite—Gallium Oxide

Effect of Gallium Oxide in Preventing Cristobalite Formation in Binary Borosilicate Glass Composite

Effect of gallium oxide on crystallization and thermal expansion behavior of low k glass composite

Devitrification Inhibitor in Binary Borosilicate Glass Composite

Crystallization kinetics of binary borosilicate glass composite

Densification Kinetics and Mechanism of a Low-Dielectric Glass Composite

Origin of cristobalite formation during sintering of a binary mixture of borosilicate glass and high silica glass

Effect of Alumina on Densification of Binary Borosilicate Glass Composite

Effects of Borosilicate Glass on Densification and Properties of Borosilicate Glass + TiO2 Ceramics

Effects of Mixed Alkaline Earth Oxides Additive on Crystallization and Structural Changes in Borosilicate Glasses

Floating Particles in the Melt during the Growth of <i>β</i>-Ga<sub>2</sub>O<sub>3</sub> Single Crystals Using the Czochralski Method

Crystallization of Cristobalite in Sodium Borosilicate Glass in the Presence of Cr2O3

Crystallization Kinetics and Mechanism of Low-Dielectric, Low-Temperature, Cofirable CaO-B<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub>Glass-Ceramics

Effect of Crystallizable Cordierite Glass on Devitrification of Pyrex Borosilicate Glass

Regulation of Y2O3 on glass stability of Ga2O3-rich oxyfluoride glasses

Floating Particles in the Melt during the Growth of <i></i>-Ga<sub>2</sub>O<sub>3</sub> Single Crystals Using the Czochralski Method

Floating Particles in the Melt during the Growth of β-Ga2O3 Single Crystals Using the Czochralski Method

Enhancing fluorescence properties in transparent glass ceramics via optimized Gd2O3/Ga2O3 ratios and crystallization conditions

Low-fire Processing and Dielectric Properties of a Binary Crystallizable Glasses+alumina System

Effect of different carbon materials on the structure and glass crystallization temperature, wettability, and expansion coefficient properties of glass

Control of nucleation and crystal growth of a silicate apatitic phase in a glassy matrix