Abstract:Kinetics of cristobalite precipitation in a binary glass composite, containing a low-softening borosilicate (BSG) and a high-softening high silica (HSG) glass, have been investigated. XRD results show that the pure glasses do not crystallize under the sintering conditions used, but when mixed in appropriate proportions the cristobalite gradually precipitates out of the initial amorphous binary glass mixture as the sintering continues at temperatures ranging from 800 to 1000-degrees-C. Average linear thermal expansion coefficient (TCE) results show that the TCE increases significantly with increasing precipitation of cristobalite as a function of sintering time. Comparing the experimental TCE results with those theoretically calculated, it is concluded that the precipitation originates most likely in the HSG rather than in the BSG. The precipitation kinetics follow the Avrami equation, and the results show an apparent activation energy of 82 kJ/mol which is close to those for the diffusion of alkali ions in silicate glasses, suggesting mass-transport controlled kinetics. The values of the Avrami exponent are 1.7-1.8, which could be interpreted as a 3-dimension diffusional growth at zero nucleation rate. The linear growth rates of cristobalite, calculated from the precipitation curve, are in the range of 4-8 X 10(-5) mum/min, and show slight temperature dependence from 800 to 1000-degrees-C. The linear growth rates of cristobalite are also calculated theoretically using the equation derived by Turnbull et al.,2 and the data are 0-3 orders of magnitude smaller than those observed experimentally. This disparity is attributed to the catalytic effect of the OH and O in air and in the glass network, as well as the diffusion of alkali ions from BSG to HSG.

Densification Kinetics and Mechanism of a Low-Dielectric Glass Composite

Densification Kinetics of Binary Borosilicate Glass Composite

Effect of Alumina on Densification of Binary Borosilicate Glass Composite

Effects of Borosilicate Glass on Densification and Properties of Borosilicate Glass + TiO2 Ceramics

Low-fire Processing and Dielectric Properties of a Binary Crystallizable Glasses+alumina System

Crystallization kinetics of binary borosilicate glass composite

Crystallization Kinetics and Mechanism of Low-Dielectric, Low-Temperature, Cofirable CaO-B<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub>Glass-Ceramics

Liquid-phase Sintering in the Glass-Cordierite System

Effects of Alumina on Densification of a Low-Temperature Cofired Crystalllizable Glass+Alumina System

Devitrification Kinetics and Mechanism of K2O-CaO-SrO-BaO-B2O3-SiO2 Glass-Ceramic

Devitrification Inhibitor in Binary Borosilicate Glass Composite

Crystallization Kinetics and Dielectric Properties of a Low‐Fire CaO–Al2O3–SiO2 Glass + Alumina System

The Effect of Applied Stress on the Densification of a Low‐Temperature Cofired Ceramic‐Filled Glass System under Constrained Sintering

Crystal Growth Inhibitor in Binary Borosilicate Glass Composite—Gallium Oxide

Sintering Densification Behaviors and Crystallization Characteristics of Glass–ceramics Formed by Two Types of CaO–B2O3–SiO2 Glass

Effects of Alumina on Devitrification Kinetics and Mechanism of K2O–CaO–SrO–BaO–B2O3–SiO2 Glass

Effects of CaO–B2O3 Glass on Sintering and Microwave Properties of Cordierite Ceramics for Low-Temperature Cofired Ceramics

Microwave dielectric characterization and densification mechanism analysis of CaO‐B2O3‐SiO2 glass‐ceramic/Al2O3 composites for LTCC applications

Microstructure and dielectric properties of glass/Al 2 O 3 composites with various low softening point borosilicate glasses

Different Microstructure BaO–B2O3–SiO2 Glass/ceramic Composites Depending on High-Temperature Wetting Affinity

Effect of Gallium Oxide in Preventing Cristobalite Formation in Binary Borosilicate Glass Composite