Abstract:To minimize crack susceptibility, a laser hybrid induction modification (LHIM) technique, involving the lowest laser energy required for continuously remelting at a preset inducting heating temperature, was used to partially remelt atmospheric plasma spraying (APS) yttria stabilized zirconia (YSZ) coating. Computational fluid dynamics (CFD) simulations indicate that a combination of elevated preheating temperature and low laser energy is essential to lower the cooling rate and temperature gradient and increase the solidification rate of melt pool. This is consistent with the experimental results obtained by eliminating the undesirable monoclinic phase and achieving the desired columnar and equiaxed grains. More importantly, the intersplat pores are healed to a higher degree, and the APS coatings become denser. These obvious structural changes decrease the differential shrinkage rate, mainly responsible for the initiation of cracks existing between the remelted layer and residual APS coatings during laser thermal shock. The healing of intersplat pores is also helpful for achieving less interfacial imperfections in the expansion of molten pool, thus developing a well-bonded remelted layer. Thus, a significantly decreased mismatch strain resulting from the lower thermal gradient and reduced differential shrinkage rate produces an acceptably low stress level for the crack susceptibility of remelted coating. Instead, the stress relief related to splat sliding is beneficial to achieve enlarged intercolumn gaps with high strain tolerance.

Laser Re-Melting Assisted with Induction Heating of Yttria Partially Stabilized Zirconia Thermal Barrier Coatings

Analysis of Ultrasonic-Assisted Laser Re-Melting of Thermal Barrier Coatings

Microstructure Evolution in Yttria Stabilized Zirconia During Laser Hybrid Induction Modification

Laser remelting of plasma-sprayed yttria partially stabilized zirconia coatings

Influence of Preheating Processes on the Microstructure of Laser Glazed YSZ Coatings

Influence of Preheating on the Microstructure Evolution of Laser Re-Melting Thermal Barrier Coatings/Ni-Based Single Crystal Superalloy Multilayer System

Single-step laser sintering of YSZ powder-beds to TBC applications

The Effects of Induction Plasma Spheroidization on the Properties of Yttrium-Stabilized Zirconia Powders and the Performance of Corresponding Thermal Barrier Coatings for Gas Turbine Engine Applications

Improving Molten CMAS Resistance of Thermal Barrier Coatings by Modified Laser Remelting Method

Molten salt corrosion behavior of laser remelted PS-PVD YSZ thermal barrier coatings

Effects of Laser Remelting and Laser Modification on the Oxidation Resistance of 8％Y2o3-Zro2 Thermal Barrier Coatings

On the oxygen vacancy annealing in air plasma sprayed YSZ thermal barrier coatings

Laser Remelting of Plasma Sprayed Nicraly and Nicraly-Al2o3 Coatings

Effects of Induction Plasma Spheroidization on Properties of Yttria-Stabilized Zirconia Powders for Thermal Barrier Coating Applications

Evaluation of Microstructural Evolution and Corrosion Types in Ultrasonic Assisted Laser Re-Melted Thermal Barrier Coatings under Exposure to Molten Salts

Heating and Melting State of YSZ Particles in Supersonic Atmospheric Plasma Spraying

A Direct Laser Sintering Approach for the Electrophoretic Deposition Overlay of Yttria-Stabilized Zirconia on the Surface of a Thermal Barrier Coating System

An investigation on the microstructure and oxidation behavior of laser remelted air plasma sprayed thermal barrier coatings

Understanding the Heat Transfer and Solidification of Plasma-Sprayed Yttria-Partially Stabilized Zirconia Coatings

High‐temperature thermal conductivity measurement of porous ceramic coatings with a high heat flux CO2 laser rig