Abstract:The results of a study of the influence of the introduction of powders of intermetallic compounds of various compositions obtained by self-propagating high-temperature synthesis (SHS) with preliminary mechanical activation on the structure, mechanical, and tribological properties of sintered bronze are presented. It was found that the introduction of 0.2–0.5 wt % of nickel and titanium aluminides, both single-phase and two-phase, leads to an increase in the density and strength of sintered bronze; maximum strength is achieved with the introduction of 0.2 wt % aluminides. The dependence of the hardness of powder bronze on the amount and composition of the intermetallic compound differs from the dependence of strength; with the introduction of single-phase intermetallic compounds, the hardness increases with increasing additive content, and with two-phase intermetallic compounds it decreases. It has been shown that the introduction of aluminides ensures a refinement of the structure of the bronze during sintering, and at an additive content of 1 wt %, an increase in the amount of eutectoid (α + δ). The introduction of aluminides also has a positive effect on the tribological properties of sintered bronze. With the introduction of 0.5 wt % two-phase nickel aluminide and 0.2 wt % single-phase titanium aluminide, the seizure pressure and wear resistance increase by 2.8 times and 3.5 times, respectively. Adding 0.5 wt % of single-phase nickel, titanium, and iron aluminides allows reducing the friction coefficient to 0.009–0.011, and two-phase iron aluminide to 0.005. The introduction of iron aluminides most effectively increases the tribological properties of sintered bronze, so the seizure pressure increases to 10 MPa and wear resistance by almost 10 times. Aluminides help reduce the relief of the friction surface during adhesive wear of sintered bronze and the formation of microlacunae, which are additional reservoirs for lubrication. The smoothest friction surface and a higher content of microlacunae are observed in samples made of powder bronze with the addition of single-phase iron aluminide.

Influence of Composite Surfactant on Print Gloss of Bronze Powder

Siloxane-modified Polyester:Synthesis and Features of Its Powder Coatings

A Comparative Investigation of the Tribological Behavior and Wear Mechanism of Bronze-graphite Composite under Dry- and Water-lubricated Sliding Against Steel

Surface Finishing and Coating Parameters Impact on Additively Manufactured Binder-Jetted Steel–Bronze Composites

Effect of Silane Coupling Agent Modification on Properties of Brass Powder-Water-Based Acrylic Coating on Tilia europaea

Suspension Swelling Graft Copolymerization of Acrylonitrile-Chlorinated Polyethylene-Styrene:Function of Composite Suspending Agents

Preparation of Bronze (CuSn10) Parts by Material Extrusion Process Using Paraffin-Based Binder

Effect of print orientation and bronze existence on tribological and mechanical properties of 3D-printed bronze/PLA composite

Influence of Coalescent on the Gloss of Plastic Water-Based Flexographic Ink

Application of Composite Powders Recycled from Graphite Tailings in Styrene-Butadiene Rubber

Exploration into Anticorrosive Property of Antirust Compound-Admixture

Influences of Tin Oxide Surface Modification on the Morphology and Performance of Sintered Ag/SnO2 Composite Powders

Influence of Ultrafine Additives of Intermetallides on the Structure, Mechanical, and Tribotechnical Properties of Sintered Tin Bronze

Comparative study of the efficiency of inhibitors and coatings for bronze artifacts

SYNERGISTIC EFFECT OF CORROSION INHIBITION ON BRONZE BY BENZOTRIAZOLE AND SODIUM MOLYBDATE

Study on the Effect of Additives on the Performance of Cement-Based Composite Anti-Corrosion Coatings for Steel Bars in Prefabricated Construction

The Glossiness Influence Factor Analysis of Flexographic Printing Water-Based Ink

The Effect of Silver Nanoparticles/Titanium Dioxide in Poly(acrylic acid- co-acrylamide)-Modified, Deproteinized, Natural Rubber Composites on Dye Removal

Impact of Optimal Silane Concentration on the Rheological Properties and 3D Printing Performance of Al2O3-Acrylate Composite Slurries

Optimization of tin and aluminum content in tin bronze according to mechanical properties indicators

Investigation of the Wettability Properties of Different Textured Lead/Lead-Free Bronze Coatings